摘要:
A method of producing a surface sizing composition, the method comprising: providing a metal salt having at least 3 valence electrons, wherein the metal salt is selected from the group of aluminium sulfate, aluminium chloride, aluminium nitrate, polyaluminium sulfate (PAS), polyaluminium chloride (PAC), and polyaluminium chloride sulfate (PACS), polyaluminium formiate, polyaluminium nitrate, and any combination thereof; providing an aqueous polymer dispersion, wherein the aqueous polymer dispersion is an aqueous polymer dispersion (A) and an aqueous prepolymer composition (B), wherein the aqueous polymer dispersion (A) is obtainable by free radical emulsion copolymerizing a first ethylenically unsaturated monomer blend, and wherein the aqueous prepolymer composition (B) is obtainable by free radical emulsion copolymerizing in a polymerization solvent comprising C1-6-carboxylic acid and C1-6-carboxylic acid anhydride, a second ethylenically unsaturated monomer blend; and mixing the metal salt and the aqueous polymer dispersion to provide a surface sizing composition to be used in papermaking.
摘要:
The present invention relates to a sizing composition that, when applied to paper substrate, creates a substrate, preferably suitable for inkjet printing, having increased print density, print sharpness, low HST, and/or image dry time, the substrate preferably having high brightness and reduced color-to-color bleed as well. In addition, the present invention relates to a method of reducing the HST of a paper substrate by applying the sizing composition to at least one surface thereof. Further, the application relates to methods of making and using the sizing composition, as well as methods of making and using the paper containing the sizing composition.
摘要:
The present invention relates to a sizing composition that, when applied to paper substrate, creates a substrate, preferably suitable for inkjet printing, having increased print density, print sharpness, low HST, and/or image dry time, the substrate preferably having high brightness and reduced color-to-color bleed as well. In addition, the present invention relates to a method of reducing the HST of a paper substrate by applying the sizing composition to at least one surface thereof. Further the application relates to methods of making and using the sizing composition, as well as methods of making and using the paper containing the sizing composition.
摘要:
The present invention relates to the field of rotogravure printing, and more specifically to a rotogravure printing medium, a coating composition for rotogravure printing media, a method for producing such a rotogravure printing medium and an use of the rotogravure printing medium in a printing application, preferably in rotogravure printing using electrostatic assist (ESA).
摘要:
The present invention relates to a dispersion for manufacturing of resin-impregnated papers, as can be used for the manufacturing of abrasion-resistant (micro scratch-resistant) surfaces, such as laminate floors, furniture surfaces or laminates (CPL, HPL). The invention relates also to a corresponding method for manufacturing of such surfaces as well as to corresponding manufactured products. Thereby, the dispersion contains for example (in weight percent) 30 to 75% water and 10 to 65% corundum particles with a particle size of F400 to F2000 as well as further additives in small quantity. This dispersion can be introduced into a liquid amino resin mixture to impregnate paper.
摘要:
The present disclosure provides a stable aqueous composition comprising an aqueous component, a hydrophobic complex comprised of a multivalent metal salt complexed with nanocellulose fibers and lignin, with the composition exhibiting a viscosity sufficient to prevent coalescing and settling of the hydrophobic complex in the aqueous component. The composition may be used to coat surfaces of articles to produce a hydrophobic surface. Once applied to the surface, the aqueous coating is spread to form a wet film covering the surface and is then dewatered and dried to produce a dried hydrophobic coating.
摘要:
An inkjet printable media comprises a paper base containing a surface coating comprising calcium chloride and a synergistic amount of a sulfate salt. When the printable media is printed with an inkjet ink containing a black pigment, a KOD value of the printed media is equal to or greater than that of a comparative inkjet printed media comprising up to 12 kg calcium chloride/T media and lacking the sulfate salt.
摘要:
A coating composition may include kaolin having a shape factor less than about 70 and calcium carbonate, wherein less than about 90% by weight and greater than about 60% by weight of particles of the calcium carbonate have an equivalent spherical diameter (esd) less than 2 microns. The coating composition may include a thickener present in an amount ranging from about 0.1% to about 0.9% by active dry weight of the composition. A coating composition may include kaolin having a shape factor less than about 70 and calcium carbonate having a mean particle size (d50) of at least about 2.4 microns and a steepness factor of at least about 30. The coating composition may be a paper basecoat composition or a paperboard basecoat composition. A paper or paperboard product may include the coating composition on at least one surface of the paper product or paperboard product.
摘要:
The present invention relates to polyoxometalate-coated alumina trihydrate dispersants prepared by combining a polyaluminum chloride having certain characteristics with alumina trihydrate particles. Such dispersants are useful for forming cationic alumina trihydrate slurries, which can be mixed with titanium dioxide to produce stable cationic slurry blends useful in paper, paper-board, and paint (coatings) applications. The dispersants are also useful for preparing cationic titanium dioxide slurries.