摘要:
A heat-conductive silicone composition comprising at least (A) an organopolysiloxane, (B) a heat-conductive filler, and (C) a specific organosiloxane. The silicone composition is excellent in handleability, even when it contains a large amount of a heat-conductive filler for the purpose of attaining higher heat conductivity.
摘要:
An oligosiloxane having the formula (R1O)aSi(OSiR22R3)4−a wherein R1 is alkyl; each R2 is independently selected from C1 to C10 monovalent hydrocarbyl free of aliphatic unsaturation; R3 is hydrocarbly free of aliphatic unsaturation and having at least 11 carbon atoms; and a is 1, 2, or 3; and a method of preparing an alkoxy-functional oligosiloxane.
摘要:
A thermally conductive silicone rubber composition, comprising (A) a curable organopolysiloxane (B) a curing agent; and (C) a filler prepared by treating the surface of a thermally conductive filler with an oligosiloxane having a formula selected from (i) (R1O)aSi(OSiR23)(4−a) and (ii) (R1O)aR2(3−a)SiO[R22SiO]nSi(OSiR23)bR2(3−b) wherein R1 is alkyl, each R2 is independently a monovalent hydrocarbon group free of aliphatic unsaturation, subscript a is an integer from 1 to 3, b is an integer from 1 to 3, and n is an integer having a value greater than or equal to 0.
摘要:
A room-temperature-curable organopolysiloxane composition comprising: (A) an organopolysiloxane having 1.5 or more end groups having at least one hydroxyl group on the average; (B) a silane or a siloxane oligomer having three or more silicon-bonded hydrolyzable groups; (D) an inorganic powder; and either (C) microparticles of thermoplastic resin containing a platinum compound having an average diameter from 0.1 to 20 μm; or (C1) a platinum compound; and (C2) an organosiloxane oligomer which contains aryl and alkenyl groups and has 8 or less silicon atoms in each molecule and which contains in each molecule at least one divalent organosiloxane as represented by the formula: —(R2)(R3)SiO—(R2)(R3)Si—, (where R2 is an aryl group, and R3 is an alkenyl group), in a quantity of at least 2 moles of component (C2) per 1 mole platinum atoms in component (C1).
摘要:
A room-temperature-curable organopolysiloxane composition comprising: (A) an organopolysiloxane having 1.5 or more end groups having at least one hydroxyl group on the average; (B) a silane or a siloxane oligomer having three or more silicon-bonded hydrolyzable groups; (D) an inorganic powder; and either (C) microparticles of thermoplastic resin containing a platinum compound having an average diameter from 0.1 to 20 μm; or (C1) a platinum compound; and (C2) an organosiloxane oligomer which contains aryl and alkenyl groups and has 8 or less silicon atoms in each molecule and which contains in each molecule at least one divalent organosiloxane as represented by the formula: —(R2)(R3)SiO—(R2)(R3)Si—, (where R2 is an aryl group, and R3 is an alkenyl group), in a quantity of at least 2 moles of component (C2) per 1 mole platinum atoms in component (C1).
摘要:
A room-temperature-curable organopolysiloxane composition comprising: (A) 100 parts by weight of an organopolysiloxane having a viscosity of from 100 to 500,000 mPa·s at 25° C. and having in one molecule 1.5 or more end groups represented by the general formula: (X)aR13-aSi—, where each X is independently a hydroxyl group or a hydrolyzable group, each R1 is independently a monovalent hydrocarbon group or a halogen-substituted monovalent hydrocarbon group, and a is 1, 2, or 3; (B) 0.01 to 40 parts by weight of a cross-linking agent selected from a silane or a siloxane oligomer where the cross-linking agent has three or more silicon-bonded hydrolyzable groups per molecule; and (C) microparticles of thermoplastic resin containing a platinum compound in such an amount that the content of metallic platinum in component (C) is within the range of 0.01 to 5 wt. %, where the microparticles have an average diameter from 0.1 to 20 μm, component (C) is present in an amount sufficient to provide 1 to 2,000 ppm of metallic platinum in the composition; and (D) 5 to 300 parts by weight of an inorganic powder.
摘要:
A composition includes: (I) an alkenyl functional, phenyl-containing polyorganosiloxane, an Si—H functional phenyl-containing polyorganosiloxane, or a combination thereof; (II) a hydrogendiorganosiloxy terminated oligodiphenylsiloxane having specific molecular weight, an alkenyl-functional, diorganosiloxy-terminated oligodiphenylsiloxane having specific molecular weight, or a combination thereof; and (III) a hydrosilylation catalyst. A light emitting device is made by applying the composition onto a light source followed by curing. The composition provides a cured material with mechanical properties suited for use as an encapsulant for a light emitting device.
摘要:
A method of manufacturing a layered silicone composite material comprising the steps of: applying a second addition-curable organopolysiloxane composition that contains a second adhesion promoter onto a first silicone layer that is formed by curing a first addition-curable organopolysiloxane composition containing a first adhesion promoter and where the first silicone layer has a hardness of less than JIS A 50; and forming a second silicone layer that has hardness of JIS A 50 or more by curing said second addition-curable organopolysiloxane composition.
摘要翻译:一种制备层状硅氧烷复合材料的方法,包括以下步骤:将含有第二粘合促进剂的第二可加成固化的有机聚硅氧烷组合物施加到通过固化含有第一粘合促进剂的第一可加成固化的有机聚硅氧烷组合物形成的第一硅氧烷层上 并且其中第一硅氧烷层具有小于JIS A 50的硬度; 并通过固化所述第二可加成固化的有机基聚硅氧烷组合物形成硬度为JIS A 50或更高的第二硅氧烷层。
摘要:
A curable organopolysiloxane composition includes: (A) a straight-chain organopolysiloxane having per molecule at least two silicon-bonded alkenyl groups and at least one silicon-bonded aryl group; (B) a branched-chain organopolysiloxane with siloxane units represented by the following general formula: RSiO3/2, where R is a substituted or unsubstituted monovalent hydrocarbon group, and having per molecule at least one silicon-bonded alkenyl group and at least one silicon-bonded aryl group; (C) an organopolysiloxane having in one molecule at least two silicon-bonded hydrogen atoms; and (D) a hydrosilylation catalyst; and a semiconductor device with a semiconductor element coated with a cured body of the aforementioned composition.
摘要:
A curable organopolysiloxane composition and an optical semiconductor element sealant, each comprising (A) a diorganopolysiloxane that has at least 2 alkenyl groups wherein at least 70 mole % of all the siloxane units are methylphenylsiloxane units and the total content of 1,3,5-trimethyl-1,3,5-triphenylcyclotrisiloxane and 1,3,5,7-tetramethyl-1,3,5,7-tetraphenylcyclotetrasiloxane is no more than 5 weight %, (B) an organopolysiloxane that has at least 2 silicon-bonded hydrogen atoms wherein at least 15 mole % of the silicon-bonded organic groups are phenyl groups, and (C) a hydrosilylation reaction catalyst. An optical semiconductor device in which an optical semiconductor element within a housing is sealed with the cured product from the aforementioned composition.