摘要:
Zeolites, improved methods for their synthesis, and catalysts, systems, and methods of using these zeolites as catalysts are described. The method of synthesis of the zeolites includes forming a mixture including a zeolitic precursor material and a structure directing agent and subjecting the mixture to high shear processing conditions.
摘要:
Zeolite catalysts and systems and methods for preparing and using zeolite catalysts having the CHA crystal structure are disclosed. The catalysts can be used to remove nitrogen oxides from a gaseous medium across a broad temperature range and exhibit hydrothermal stable at high reaction temperatures. The zeolite catalysts include a zeolite carrier having a silica to alumina ratio from about 15:1 to about 256:1 and a copper to alumina ratio from about 0.25:1 to about 1:1.
摘要:
Zeolite catalysts and systems and methods for preparing and using zeolite catalysts having the CHA crystal structure are disclosed. The catalysts can be used to remove nitrogen oxides from a gaseous medium across a broad temperature range and exhibit hydrothermal stable at high reaction temperatures. The zeolite catalysts include a zeolite carrier having a silica to alumina ratio from about 15:1 to about 256:1 and a copper to alumina ratio from about 0.25:1 to about 1:1.
摘要:
Zeolite catalysts and systems and methods for preparing and using zeolite catalysts having the CHA crystal structure are disclosed. The catalysts can be used to remove nitrogen oxides from a gaseous medium across a broad temperature range and exhibit hydrothermal stable at high reaction temperatures. The zeolite catalysts include a zeolite carrier having a silica to alumina ratio from about 15:1 to about 256:1 and a copper to alumina ratio from about 0.25: 1 to about 1:1.
摘要:
Disclosed herein are compositions comprising an aluminosilicate zeolite crystals with an 8 ring pore size having a depth dependent silica to alumina molar ratio and processes of making aluminosilicate zeolite crystals with an 8 ring pore size having a depth dependent silica to alumina molar ratio.
摘要:
The hydroisomerization of a paraffinic hydrocarbon feedstock obtained from renewable sources is effectively achieved by passing the feedstock in the presence of hydrogen over a hydroisomerization catalyst comprising a crystalline metal silicate molecular sieve, in which a portion of the crystalline framework contains iron.
摘要:
Described are catalyst compositions, catalytic articles, methods of manufacturing catalytic articles and exhaust gas treatment systems and methods that utilize the catalytic articles. The catalytic articles include a washcoat of platinum group metal on refractory oxide support particles, and further including a molecular sieve wherein greater than 90% of the molecular sieve particles have a particle size greater than 1 μm.
摘要:
Zeolite catalysts and systems and methods for preparing and using zeolite catalysts having the CHA crystal structure are disclosed. The catalysts can be used to remove nitrogen oxides from a gaseous medium across a broad temperature range and exhibit hydrothermal stable at high reaction temperatures. The zeolite catalysts include a zeolite carrier having a silica to alumina ratio from about 15:1 to about 256:1 and a copper to alumina ratio from about 0.25:1 to about 1:1.
摘要:
The hydroisomerization of a paraffinic hydrocarbon feedstock obtained from renewable sources is effectively achieved by passing the feedstock in the presence of hydrogen over a hydroisomerization catalyst comprising a crystalline metal silicate molecular sieve, in which a portion of the crystalline framework contains iron.
摘要:
Disclosed are storage vessel pressurization components and methods for use with a storage vessel having a headspace with a first gaseous species. The storage vessel pressurization component including a storage medium with a second gaseous species adsorbed thereon. The storage vessel pressurization component configured to adsorb the first gaseous species from the headspace and release the second gaseous species into the headspace. Articles comprising the storage vessel pressurization component are also described.