摘要:
A process for making a latex emulsion suitable for use in a toner composition includes contacting at least one amorphous polyester resin with a viscosity reducing additive in the absence of an organic solvent to form a resin mixture either via an extruder or batch process, and adding a surfactant, neutralizing agent, and deionized water to the resin mixture.
摘要:
A process for making a latex emulsion suitable for use in a toner composition includes contacting at least one polyester resin with a bio-based solvent to form a resin mixture, adding a neutralizing agent and deionized water to the resin mixture, removing the solvent from the formed latex, and recovering the emulsion. The solvent removed from the formed latex may be re-used, making the process very environmentally friendly.
摘要:
Various solvent-assisted extrusion processes are disclosed that are suitable for forming high yield, low coarse content, polyester latexes that may be utilized in forming a toner.
摘要:
A process for making a latex emulsion suitable for use in a toner composition includes contacting at least one amorphous polyester resin with a viscosity reducing additive in the absence of an organic solvent to form a resin mixture either via an extruder or batch process, and adding a surfactant, neutralizing agent, and deionized water to the resin mixture.
摘要:
A method of making toner particles, including: mixing, at less than about 17° C. and without homogenizing, a resin emulsion with a coagulant, a colorant, an optional wax, and optional additives, to form pre-aggregated particles in a slurry; heating the slurry to form aggregated toner particles; freezing aggregation of the particles in the slurry once at a desired aggregated particle size; and further heating the aggregated particles in the slurry to coalesce the aggregated particles into toner particles.
摘要:
A process and system for continuously making a resin emulsion suitable for use in forming toner particles includes at least one micromixer for micromixing a resin mixture and aqueous phase to continuously produce an emulsion of a high solids content. The process comprises contacting a polyester resin possessing acid groups with a component selected from the group consisting of an organic solvent and a solvent inversion agent to form a resin mixture; neutralizing the resin mixture with a neutralizing agent; and subjecting the resin mixture to micromixing.
摘要:
A process for making a resin emulsion suitable for use in forming toner particles is provided. In embodiments, a suitable process includes melt mixing a resin in the absence of an organic solvent, optionally adding a surfactant to the resin, adding to the resin a basic agent and water, and subjecting the resin, basic agent and water to acoustic mixing at a suitable frequency to form an emulsion of resin particles. In embodiments, the resin emulsion thus produced may be utilized to form a toner.
摘要:
A process for making a self-emulsifying granule suitable for use in forming latex emulsions includes contacting a resin with a solid or highly concentrated surfactant, a solid neutralization agent and water in the absence of an organic solvent to form a mixture, melt mixing the mixture, and forming self-emulsifying granules of the melt mixed mixture. Self-emulsifying granules are also provided and configured to form a latex emulsion when added to water, which may then be utilized to form a toner.
摘要:
A process for making a self-emulsifying composite suitable for use in forming latex emulsions includes contacting a resin with a solid or highly concentrated surfactant, a solid neutralizing agent in the absence of water and an organic solvent to form a mixture, melt mixing the mixture, and forming a self-emulsifying composite of the melt mixed mixture such as a granule. Self-emulsifying granules are also provided and configured to form a latex emulsion when added to water, which may then be utilized to form a toner.
摘要:
The present disclosure provides processes for reducing the particle size of latex resins and toners produced with such resins. In embodiments, a gel latex may be formed as a seed particle and then utilized to form latex resins and toner particles. In accordance with the present disclosure, one may be able to utilize materials for the production of latex resins and toners which may otherwise produce particles that are too large in the absence of the gel latex.