摘要:
This cold-rolled steel sheet includes, in terms of mass %, C: not less than 0.05% and not more than 0.095%, Cr: not less than 0.15% and not more than 2.0%, B: not less than 0.0003% and not more than 0.01%, Si: not less than 0.3% and not more than 2.0%, Mn: not less than 1.7% and not more than 2.6%, Ti: not less than 0.005% and not more than 0.14%, P: not more than 0.03%, S: not more than 0.01%, Al: not more than 0.1%, N: less than 0.005%, O: not less than 0.0005% and not more than 0.005%, and contains as the remainder, iron and unavoidable impurities, wherein the microstructure of the steel sheet includes mainly polygonal ferrite having a crystal grain size of not more than 4 μm, and hard microstructures of bainite and martensite, the block size of the martensite is not more than 0.9 μm, the Cr content within the martensite is 1.1 to 1.5 times the Cr content within the polygonal ferrite, and the tensile strength is at least 880 MPa.
摘要:
This cold-rolled steel sheet includes, in terms of mass %, C: not less than 0.05% and not more than 0.095%, Cr: not less than 0.15% and not more than 2.0%, B: not less than 0.0003% and not more than 0.01%, Si: not less than 0.3% and not more than 2.0%, Mn: not less than 1.7% and not more than 2.6%, Ti: not less than 0.005% and not more than 0.14%, P: not more than 0.03%, S: not more than 0.01%, Al: not more than 0.1%, N: less than 0.005%, O: not less than 0.0005% and not more than 0.005%, and contains as the remainder, iron and unavoidable impurities, wherein the microstructure of the steel sheet includes mainly polygonal ferrite having a crystal grain size of not more than 4 μm, and hard microstructures of bainite and martensite, the block size of the martensite is not more than 0.9 μm, the Cr content within the martensite is 1.1 to 1.5 times the Cr content within the polygonal ferrite, and the tensile strength is at least 880 MPa.
摘要:
Hot rolled steel sheet which has a maximum tensile strength of 600 MPa or more and has an excellent low temperature impact energy absorption and HAZ softening resistance and a method of production of the same are provided, that is, sheet which contains, by mass %, C: 0.04 to 0.09%, Si: 0.4% or less, Mn: 1.2 to 2.0%, P: 0.1% or less, S: 0.02% or less, Al: 1.0% or less, Nb: 0.02 to 0.09%, Ti: 0.02 to 0.07%, and N: 0.005% or less, where 2.0≦Mn+8[% Ti]+12[% Nb]≦2.6, has a balance of Fe and unavoidable impurities, has an area percentage of pearlite of 5% or less, has a total area percentage of martensite and retained austenite of 0.5% or less, has a balance of a metal structure of ferrite and/or bainite, has an average grain size of ferrite and bainite of 10 μm or less, has an average particle size of alloy carbonitrides with incoherent interfaces which contain Ti and Nb of 20 nm or less, and has a yield ratio of 0.85 or more.
摘要:
This hot-rolled steel sheet contains, in terms of mass %, C: 0.015% or more to less than 0.040%; Si: less than 0.05%; Mn: 0.9% or more to 1.8% or less; P: less than 0.02%; S: less than 0.01%; Al: less than 0.1%; N: less than 0.006%; and Ti: 0.05% or more to less than 0.11%, with the remainder being Fe and inevitable impurities, wherein Ti/C is in a range of 2.5 or more to less than 3.5, Nb, Zr, V, Cr, Mo, B and W are not included, a microstructure includes a mixed microstructure of polygonal ferrite and quasi-polygonal ferrite in a proportion of greater than 96%, a maximum tensile strength is 520 MPa or more and less than 720 MPa, an aging index AI is more than 15 MPa, a product of a hole expansion ratio (λ) % and a total elongation (El) % is 2350 or more, and a fatigue limit is 200 MPa or more.
摘要:
This hot-rolled steel sheet contains, in terms of mass%, C: 0.015% or more to less than 0.040%; Si: less than 0.05%; Mn: 0.9% or more to 1.8% or less; P: less than 0.02%; S: less than 0.01%; Al: less than 0.1%; N: less than 0.006%; and Ti: 0.05% or more to less than 0.11%, with the remainder being Fe and inevitable impurities, wherein Ti/C is in a range of 2.5 or more to less than 3.5, Nb, Zr, V, Cr, Mo, B and W are not included, a microstructure includes a mixed microstructure of polygonal ferrite and quasi-polygonal ferrite in a proportion of greater than 96%, a maximum tensile strength is 520 MPa or more and less than 720 MPa, an aging index AI is more than 15 MPa, a product of a hole expansion ratio (A) % and a total elongation (El) % is 2350 or more, and a fatigue limit is 200 MPa or more.
摘要:
The invention is directed to providing, for application in automobiles, construction materials, household appliances and the like, high-strength sheets excellent in formability properties such as hole expansibility and ductility, and also in fatigue resistance, characterized in comprising, in specified contents expressed in mass %, C, Si, Mn, P, S, Al, N and O and a balance of iron and unavoidable impurities, and having a steel sheet structure composed mainly of ferrite and hard structures, a crystal orientation difference between some ferrite adjacent to hard structures and the hard structures of less than 9°, and a maximum tensile strength of 540 MPa or greater.
摘要:
The invention is directed to providing, for application in automobiles, construction materials, household appliances and the like, high-strength sheets excellent in formability properties such as hole expansibility and ductility, and also in fatigue resistance, characterized in comprising, in specified contents expressed in mass %, C, Si, Mn, P, S, Al, N and O and a balance of iron and unavoidable impurities, and having a steel sheet structure composed mainly of ferrite and hard structures, a crystal orientation difference between some ferrite adjacent to hard structures and the hard structures of less than 9°, and a maximum tensile strength of 540 MPa or greater.
摘要:
The invention is directed to providing, for application in automobiles, construction materials, household appliances and the like, high-strength sheets excellent in formability properties such as hole expansibility and ductility, and also in fatigue resistance, characterized in comprising, in specified contents expressed in mass %, C, Si, Mn, P, S, Al, N and O and a balance of iron and unavoidable impurities, and having a steel sheet structure composed mainly of ferrite and hard structures, a crystal orientation difference between some ferrite adjacent to hard structures and the hard structures of less than 9°, and a maximum tensile strength of 540 MPa or greater.
摘要:
This high-strength steel sheet includes by mass percentage: 0.05 to 0.4% of C; 0.1 to 2.5% of Si; 1.0 to 3.5% of Mn; 0.001 to 0.03% of P; 0.0001 to 0.01% of S; 0.001 to 2.5% of Al; 0.0001 to 0.01% of N; 0.0001 to 0.008% of O; and a remainder composed of iron and inevitable impurities, wherein a steel sheet structure contains by volume fraction 10 to 50% of a ferrite phase, 10 to 50% of a tempered martensite phase, and a remaining hard phase, wherein a 98% hardness is 1.5 or more times as high as a 2% hardness in a range from ⅛ to ⅜ of a thickness of the steel sheet, wherein a kurtosis K* of the hardness distribution between the 2% hardness and the 98% hardness is −1.2 to −0.4, and wherein an average crystal grain size in the steel sheet structure is 10 μm or less.
摘要:
This high-strength steel sheet includes by mass percentage: 0.05 to 0.4% of C; 0.1 to 2.5% of Si; 1.0 to 3.5% of Mn; 0.001 to 0.03% of P; 0.0001 to 0.01% of S; 0.001 to 2.5% of Al; 0.0001 to 0.01% of N; 0.0001 to 0.008% of O; and a remainder composed of iron and inevitable impurities, wherein a steel sheet structure contains by volume fraction 10 to 50% of a ferrite phase, 10 to 50% of a tempered martensite phase, and a remaining hard phase, wherein a 98% hardness is 1.5 or more times as high as a 2% hardness in a range from ⅛ to ⅜ of a thickness of the steel sheet, wherein a kurtosis K* of the hardness distribution between the 2% hardness and the 98% hardness is −1.2 to −0.4, and wherein an average crystal grain size in the steel sheet structure is 10 μm or less.