公开(公告)号：US11512362B2

公开(公告)日：2022-11-29

申请号：US17087019

申请日：2020-11-02

申请人： ArcelorMittal

发明人： Olga A. Girina ,  Damon Panahi

IPC分类号： C21D9/46 ,  C21D1/22 ,  C21D6/00 ,  C21D8/02 ,  C22C38/02 ,  C22C38/04 ,  C22C38/06 ,  C23C2/06 ,  C23C2/28 ,  C23C2/40 ,  C22C38/00 ,  C23C2/02 ,  B32B15/04 ,  C22C38/44 ,  C23C2/26 ,  C23C30/00 ,  C22C38/18 ,  B32B15/01 ,  C22C38/12 ,  C23C2/34 ,  B32B15/18 ,  C22C38/22 ,  C22C38/34 ,  C22C38/38

摘要： A method for producing a coated steel sheet having a tensile strength TS of at least 1450 MPa and a total elongation TE of at least 17% includes the successive steps of providing a cold rolled steel sheet made of a steel having a chemical composition comprising, in weight %: 0.34%≤C≤0.45%, 1.50%≤Mn≤2.30%, 1.50≤Si≤2.40%, 0%

公开(公告)号：US20210222267A1

公开(公告)日：2021-07-22

申请号：US17225033

申请日：2021-04-07

申请人： ArcelorMittal

发明人： Olga A. Girina ,  Damon Panahi

IPC分类号： C21D9/46 ,  C23C2/04 ,  B32B15/04 ,  C23C30/00 ,  C23C2/12 ,  B32B15/18 ,  B32B15/00 ,  C22C38/34 ,  C21D8/04 ,  C23C2/28 ,  C25D7/06 ,  C21D8/02 ,  C21D1/25 ,  C22C38/00 ,  C22C38/02 ,  C22C38/04 ,  C22C38/06 ,  C22C38/22 ,  C22C38/38 ,  C21D1/78 ,  C21D1/19 ,  C21D9/48 ,  C22C38/18 ,  C22C38/12 ,  C21D1/18 ,  B32B15/01 ,  C25D3/22 ,  C25D5/36 ,  C25D7/00 ,  C22C38/26 ,  C23C2/06 ,  C23C2/40

摘要： A method IS for producing a cold rolled steel sheet having a tensile strength ≥1470 MPa and a total elongation TE≥19%. The method includes the steps of annealing at an annealing temperature AT≥Ac3 a non-treated steel sheet whose chemical composition contains in weight %: 0.34%≤C≤0.40%, 1.50%≤Mn≤2.30%, 1.50≤Si≤2.40%, 0%

公开(公告)号：US20190264299A1

公开(公告)日：2019-08-29

申请号：US16413111

申请日：2019-05-15

申请人： ArcelorMittal

发明人： Olga A. Girina ,  Damon Panahi

IPC分类号： C21D9/46 ,  C25D5/36 ,  B32B15/01 ,  C21D8/02 ,  C21D8/04 ,  C21D1/18 ,  B32B15/00 ,  B32B15/18 ,  B32B15/04 ,  C23C30/00 ,  C23C2/12 ,  C23C2/04 ,  C21D1/78 ,  C23C2/40 ,  C22C38/26 ,  C23C2/06 ,  C25D7/00 ,  C25D3/22 ,  C25D7/06 ,  C23C2/28 ,  C22C38/34 ,  C22C38/38 ,  C22C38/22 ,  C22C38/06 ,  C22C38/04 ,  C22C38/02 ,  C22C38/00 ,  C21D1/25

摘要： A method for producing a cold rolled steel sheet having a tensile strength≥1470 MPa and a total elongation TE≥19%, the method comprising the steps of annealing at an annealing temperature AT≥Ac3 a non-treated steel sheet whose chemical composition contains in weight %: 0.34%≤C≤0.40%, 1.50%≤Mn≤2.30%, 1.50≤Si≤2.40%, 0

公开(公告)号：US11131003B2

公开(公告)日：2021-09-28

申请号：US16413111

申请日：2019-05-15

申请人： ArcelorMittal

发明人： Olga A. Girina ,  Damon Panahi

IPC分类号： C21D9/46 ,  C25D5/36 ,  B32B15/01 ,  C21D8/02 ,  C21D8/04 ,  C23C2/04 ,  B32B15/04 ,  C23C30/00 ,  C23C2/12 ,  B32B15/18 ,  B32B15/00 ,  C22C38/34 ,  C23C2/28 ,  C25D7/06 ,  C21D1/25 ,  C22C38/00 ,  C22C38/02 ,  C22C38/04 ,  C22C38/06 ,  C22C38/22 ,  C22C38/38 ,  C21D1/78 ,  C21D1/19 ,  C21D9/48 ,  C22C38/18 ,  C22C38/12 ,  C21D1/18 ,  C25D3/22 ,  C25D7/00 ,  C22C38/26 ,  C23C2/06 ,  C23C2/40

摘要： A method for producing a cold rolled steel sheet having a tensile strength≥1470 MPa and a total elongation TE≥19%, the method comprising the steps of annealing at an annealing temperature AT≥Ac3 a non-treated steel sheet whose chemical composition contains in weight %: 0.34%≤C≤0.40%, 1.50%≤Mn≤2.30%, 1.50≤Si≤2.40%, 0%

公开(公告)号：US11035020B2

公开(公告)日：2021-06-15

申请号：US16067055

申请日：2015-12-29

申请人： ArcelorMittal

发明人： Olga A. Girina ,  Damon Panahi

IPC分类号： B32B15/01 ,  C23C2/06 ,  C23C2/28 ,  C23C2/40 ,  C22C38/38 ,  C22C38/34 ,  C22C38/22 ,  C22C38/06 ,  C21D6/00 ,  C21D9/46 ,  C21D8/02 ,  C21D1/22 ,  C22C38/00 ,  C23C2/02 ,  B32B15/04 ,  C22C38/44 ,  C23C2/26 ,  C22C38/04 ,  C23C30/00 ,  C22C38/02 ,  C22C38/18 ,  C22C38/12 ,  C23C2/34 ,  B32B15/18

摘要： A method for producing a coated steel sheet having a tensile strength of at least 1450 MPa and a total elongation of at least 17% is provided. The method includes providing a cold rolled steel sheet having a chemical composition in weight %: 0.34%≤C≤0.45%, 1.50%≤Mn≤2.30%, 1.50%≤Si≤2.40%, 0%

公开(公告)号：US11001904B2

公开(公告)日：2021-05-11

申请号：US15323311

申请日：2015-07-03

申请人： ArcelorMittal

发明人： Olga A. Girina ,  Damon Panahi

IPC分类号： C21D9/46 ,  C21D8/02 ,  C23C2/04 ,  B32B15/04 ,  C23C30/00 ,  C23C2/12 ,  B32B15/18 ,  B32B15/00 ,  C22C38/34 ,  C21D8/04 ,  C23C2/28 ,  C25D7/06 ,  C21D1/25 ,  C22C38/00 ,  C22C38/02 ,  C22C38/04 ,  C22C38/06 ,  C22C38/22 ,  C22C38/38 ,  C21D1/78 ,  C21D1/19 ,  C21D1/18 ,  B32B15/01 ,  C25D3/22 ,  C25D5/36 ,  C25D7/00 ,  C22C38/26 ,  C23C2/06 ,  C23C2/40

摘要： A method for producing a cold rolled steel sheet having a tensile strength≥1470 MPa and a total elongation TE≥19%, the method comprising the steps of annealing at an annealing temperature AT≥Ac3 a non-treated steel sheet whose chemical composition contains in weight %: 0.34%≤C≤0.40%, 1.50%≤Mn≤2.30%, 1.50≤Si≤2.40%, 0%

公开(公告)号：US12054802B2

公开(公告)日：2024-08-06

申请号：US18195578

申请日：2023-05-10

申请人： ArcelorMittal

发明人： Jean-Marc Pipard ,  Sebastien Cremel ,  Anirban Chakraborty ,  Damon Panahi ,  Olga Girina ,  Hassan Ghassemi-Armaki ,  Pavan Challa Venkata Surya ,  Yacine Benlatreche

IPC分类号： C21D9/50 ,  B23K11/11 ,  B23K11/16 ,  B23K31/12 ,  B23K37/04 ,  C21D1/76 ,  C21D6/00 ,  C21D8/02 ,  C21D9/46 ,  C22C38/02 ,  C22C38/06 ,  C22C38/22 ,  C22C38/38 ,  C23C2/02 ,  C23C2/26 ,  C23C2/40 ,  C23F17/00 ,  C25D5/36 ,  B23K101/00 ,  B23K103/04 ,  C23C2/06 ,  C25D3/22

CPC分类号： C21D9/50 ,  B23K11/115 ,  B23K11/163 ,  B23K31/125 ,  B23K37/0408 ,  C21D1/76 ,  C21D6/002 ,  C21D6/005 ,  C21D6/008 ,  C21D8/0205 ,  C21D8/0236 ,  C21D8/0247 ,  C21D9/46 ,  C22C38/02 ,  C22C38/06 ,  C22C38/22 ,  C22C38/38 ,  C23C2/02 ,  C23C2/0222 ,  C23C2/0224 ,  C23C2/024 ,  C23C2/26 ,  C23C2/40 ,  C23F17/00 ,  C25D5/36 ,  B23K2101/006 ,  B23K2103/04 ,  C21D2211/001 ,  C21D2211/008 ,  C23C2/06 ,  C25D3/22

摘要： A method for producing a zinc or zinc-alloy coated steel sheet with a tensile strength higher than 900 MPa, for the fabrication of resistance spot welds containing in average not more than two Liquid Metal Embrittlement cracks per weld having a depth of 100 μm or more, with steps of providing a cold-rolled steel sheet, heating cold-rolled steel sheet up to a temperature T1 between 550° C. and Ac1+50° C. in a furnace zone with an atmosphere (A1) containing from 2 to 15% hydrogen by volume, so that the iron is not oxidized, then adding in the furnace atmosphere, water steam or oxygen with an injection flow rate Q higher than (0.07%/h×α), α being equal to 1 if said element is water steam or equal to 0.52 if said element is oxygen, at a temperature T≥T1, so to obtain an atmosphere (A2) with a dew point DP2 between −15° C. and the temperature Te of the iron/iron oxide equilibrium dew point, then heating the sheet from temperature T1 up to a temperature T2 between 720° C. and 1000° C. in a furnace zone under an atmosphere (A2) of nitrogen containing from 2 to 15% hydrogen and more than 0.1% CO by volume, with an oxygen partial pressure higher than 10−21 atm., wherein the duration to of heating of the sheet from temperature T1 up to the end of soaking at temperature T2 is between 100 and 500 s, soaking the sheet at T2, then cooling the sheet at a rate between 10 and 400° C./s, then coating the sheet with zinc or zinc-alloy coating.

公开(公告)号：US10378077B2

公开(公告)日：2019-08-13

申请号：US15323232

申请日：2014-07-03

申请人： ArcelorMittal

发明人： Olga A. Girina ,  Damon Panahi

IPC分类号： C21D9/46 ,  C21D8/02 ,  C21D1/18 ,  C25D5/36 ,  C25D7/00 ,  C25D3/22 ,  B32B15/01 ,  C22C38/38 ,  C22C38/34 ,  C22C38/22 ,  C22C38/06 ,  C23C2/04 ,  B32B15/04 ,  C23C30/00 ,  C23C2/12 ,  B32B15/18 ,  B32B15/00 ,  C21D1/25 ,  C22C38/00 ,  C22C38/02 ,  C22C38/04 ,  C21D8/04 ,  C23C2/28 ,  C25D7/06 ,  C22C38/26 ,  C23C2/06 ,  C23C2/40

摘要： A method for producing a cold rolled steel sheet having a tensile strength ≥1470 MPa and a total elongation TE≥19%, the method comprising the steps of annealing at an annealing temperature AT≥Ac3 a non-treated steel sheet whose chemical composition contains in weight %: 0.34%≤C≤0.40%, 1.50%≤Mn≤2.30%, 1.50≤Si≤2.40%, 0%

公开(公告)号：US20170137910A1

公开(公告)日：2017-05-18

申请号：US15323311

申请日：2015-07-03

申请人： ArcelorMittal

发明人： Olga A. Girina ,  Damon Panahi

IPC分类号： C21D9/46 ,  C25D5/36 ,  C23C2/06 ,  C23C2/40 ,  B32B15/01 ,  C22C38/34 ,  C22C38/26 ,  C22C38/22 ,  C22C38/06 ,  C21D8/02 ,  C25D3/22 ,  C22C38/38

CPC分类号： C21D9/46 ,  B32B15/00 ,  B32B15/013 ,  B32B15/04 ,  B32B15/043 ,  B32B15/18 ,  C21D1/18 ,  C21D1/19 ,  C21D1/25 ,  C21D8/0236 ,  C21D8/0247 ,  C21D8/0278 ,  C21D8/0447 ,  C21D2211/001 ,  C21D2211/008 ,  C22C38/00 ,  C22C38/02 ,  C22C38/04 ,  C22C38/06 ,  C22C38/22 ,  C22C38/26 ,  C22C38/34 ,  C22C38/38 ,  C23C2/04 ,  C23C2/06 ,  C23C2/12 ,  C23C2/28 ,  C23C2/40 ,  C23C30/00 ,  C23C30/005 ,  C25D3/22 ,  C25D5/36 ,  C25D7/00 ,  C25D7/0614 ,  Y10T428/12757 ,  Y10T428/12799 ,  Y10T428/12951 ,  Y10T428/12972

摘要： A method for producing a cold rolled steel sheet having a tensile strength≧1470 MPa and a total elongation TE≧19%, the method comprising the steps of annealing at an annealing temperature AT≧Ac3 a non-treated steel sheet whose chemical composition contains in weight %: 0.34%≦C≦0.40%, 1.50%≦Mn≦2.30%, 1.50≦Si≦2.40%, 0%≦Cr≦0.7%, 0%≦Mo≦0.3%, 0.01%≦Al≦0.07%, the remainder being Fe and unavoidable impurities, quenching the annealed steel sheet by cooling it to a quenching temperature QT

公开(公告)号：US11649522B2

公开(公告)日：2023-05-16

申请号：US16614734

申请日：2018-06-13

申请人： ArcelorMittal

发明人： Jean-Marc Pipard ,  Sebastien Cremel ,  Anirban Chakraborty ,  Damon Panahi ,  Olga Girina ,  Hassan Ghassemi-Armaki ,  Pavan Challa Venkata Surya ,  Yacine Benlatreche

IPC分类号： C21D9/50 ,  C21D8/02 ,  C21D6/00 ,  C22C38/38 ,  C22C38/22 ,  C22C38/06 ,  C22C38/02 ,  C21D9/46 ,  C21D1/76 ,  C23C2/02 ,  C23C2/40 ,  C25D5/36 ,  C23F17/00 ,  B23K11/11 ,  B23K31/12 ,  B23K11/16 ,  B23K37/04 ,  B23K103/04 ,  B23K101/00 ,  C23C2/06 ,  C25D3/22

CPC分类号： C21D9/50 ,  B23K11/115 ,  B23K11/163 ,  B23K31/125 ,  B23K37/0408 ,  C21D1/76 ,  C21D6/002 ,  C21D6/005 ,  C21D6/008 ,  C21D8/0205 ,  C21D8/0236 ,  C21D8/0247 ,  C21D9/46 ,  C22C38/02 ,  C22C38/06 ,  C22C38/22 ,  C22C38/38 ,  C23C2/02 ,  C23C2/40 ,  C23F17/00 ,  C25D5/36 ,  B23K2101/006 ,  B23K2103/04 ,  C21D2211/001 ,  C21D2211/008 ,  C23C2/06 ,  C25D3/22

摘要： A method for producing a zinc or zinc-alloy coated steel sheet with a tensile strength higher than 900 MPa, for the fabrication of resistance spot welds containing in average not more than two Liquid Metal Embrittlement cracks per weld having a depth of 100 μm or more, with steps of providing a cold-rolled steel sheet, heating cold-rolled steel sheet up to a temperature T1 between 550° C. and Ac1+50° C. in a furnace zone with an atmosphere (A1) containing from 2 to 15% hydrogen by volume, so that the iron is not oxidized, then adding in the furnace atmosphere, water steam or oxygen with an injection flow rate Q higher than (0.07%/h×α), α being equal to 1 if said element is water steam or equal to 0.52 if said element is oxygen, at a temperature T≥T1, so to obtain an atmosphere (A2) with a dew point DP2 between −15° C. and the temperature Te of the iron/iron oxide equilibrium dew point, then heating the sheet from temperature T1 up to a temperature T2 between 720° C. and 1000° C. in a furnace zone under an atmosphere (A2) of nitrogen containing from 2 to 15% hydrogen and more than 0.1% CO by volume, with an oxygen partial pressure higher than 10−21 atm., wherein the duration tD of heating of the sheet from temperature T1 up to the end of soaking at temperature T2 is between 100 and 500 s., soaking the sheet at T2, then cooling the sheet at a rate between 10 and 400° C./s, then coating the sheet with zinc or zinc-alloy coating.