A precursor mixture for producing a porous body, wherein the precursor mixture comprises: (i) milled alpha alumina powder having a particle size of 0.1 to 6 microns, (ii) boehmite powder that functions as a binder of the alpha alumina powders, and (iii) burnout materials having a particle sizes of 1-10 microns. In some embodiments, an unmilled alpha alumina powder having a particle size of 10 to 100 microns is also included in said precursor mixture. Also described herein is a method for producing a porous body in which the above-described precursor mixture is formed to a given shape, and subjected to a heat treatment step in which the formed shape is sintered to produce the porous body.