公开(公告)号：US20020056648A1

公开(公告)日：2002-05-16

申请号：US09951406

申请日：2001-09-14

申请人： FUJI PHOTO FILM CO., LTD.

发明人： Hirokazu Sawada ,  Akio Uesugi ,  Atsuo Nishino ,  Yoshitaka Masuda

IPC分类号： C25D005/34 ,  C25D011/18 ,  C25D005/44 ,  C25D011/16 ,  C25D011/04

CPC分类号： C22C21/00 ,  B41N3/034

摘要： A process for producing an aluminum support for a planographic printing plate, the process comprising the steps of: (a) preparing an aluminum plate; (b) disposing said aluminum plate in an aqueous acidic solution; and (c) electrochemically surface-roughening said aluminum plate using an alternating current, wherein a ratio QC/QA of a cathode-time quantity of electricity of said aluminum plate QC to an anode-time quantity of electricity of said aluminum plate QA is from 0.95 to 2.5. An aluminum support for a planographic printing plate formed by the process. A planographic printing master plate comprising at least a positive-type or negative-type light-sensitive layer on the aluminum support.

摘要翻译： 一种用于制备平版印刷版的铝支架的方法，所述方法包括以下步骤：（a）制备铝板; （b）将所述铝板置于酸性水溶液中; 和（c）使用交流电对所述铝板进行电化学表面粗糙化，其中所述铝板QC的阴极时间电量与所述铝板QA的阳极时间电量的比值QC / QA来自 0.95〜2.5。 用于通过该方法形成的平版印刷版的铝支架。 平版印刷母板，其在铝支架上至少包括正型或负型光敏层。

公开(公告)号：US20010038908A1

公开(公告)日：2001-11-08

申请号：US09801781

申请日：2001-03-09

发明人： Masaya Matsuki ,  Yoshinori Hotta ,  Hirokazu Sawada ,  Akio Uesugi

IPC分类号： B32B003/00 ,  B41N001/06 ,  C25D011/16 ,  C25F003/04 ,  G03F007/09

CPC分类号： B41N3/03 ,  B41N1/083 ,  B41N3/034 ,  Y10T428/249921 ,  Y10T428/266

摘要： A substrate for a planographic printing plate and a method of fabrication thereof. After a surface roughening treatment and before an anodizing treatment, an aluminum alloy plate to be used as the substrate is washed in an alkali solution, and then in an acidic solution. After surface-roughening, overlap points of Fe and Si macularly distributed at the surface of the aluminum alloy plate have a surface coverage of not more than 0.5%, and there are no more than 800 per 1 mm2 of overlap points which have sizes larger than 1.6null10null7 mm2. The planographic printing plate of the present invention has excellent printing capabilities in that, irrespective of printing conditions, soiling does not occur at a non-image portion of the planographic printing plate.

摘要翻译： 平版印刷版用基板及其制造方法。 在表面粗糙化处理之后和阳极氧化处理之前，将用作基材的铝合金板在碱溶液中洗涤，然后在酸性溶液中洗涤。 在表面粗糙化之后，在铝合金板表面上黄色分布的Fe和Si的重叠点的表面覆盖率不大于0.5％，并且每1mm 2重叠点不超过800个，其重量大于 1.6x10-7 mm2。 本发明的平版印刷版具有出色的印刷能力，不论打印条件如何，在平版印刷版的非图像部分都不会发生污染。

公开(公告)号：US20020096434A1

公开(公告)日：2002-07-25

申请号：US09766356

申请日：2001-01-19

发明人： Gregory S. Marczak ,  Rick A. Minner

IPC分类号： C25D005/00 ,  C25D005/44 ,  C25D011/16 ,  C25D011/04 ,  C25D007/06

CPC分类号： C25D11/22

摘要： A process and apparatus for conducting an electrically independent current through an anodized web to electro-deposit a coloring agent on the web. A preferred process includes the step of providing a continuous web of anodized aluminum; transferring with a charging plate a coloring current to the web with a charging plate in a first treatment cell over an area of the web sufficient to allow the current to pass through an anodic layer of the aluminum and flow through the web; and electro-depositing coloring agents on the web with the coloring current in a second treatment cell. Optionally, the web may be serially passed through additional treatment cells to apply a variety of different coloring currents to the web whereby the web may be colored with multiple coloring agents and consequently exhibit multiple colors and/or refractive properties.

摘要翻译： 一种用于通过阳极氧化网进行电独立电流以在网上电沉积着色剂的方法和装置。 优选的方法包括提供阳极氧化铝的连续纤维网的步骤; 用充电板将着色电流转移到幅材上，在第一处理电池中的充电板在幅材的区域上足以允许电流通过铝的阳极层并流过幅材; 以及在第二处理池中具有着色电流在网上电沉积着色剂。 任选地，纤维网可以连续地通过另外的处理细胞，以将多种不同的着色电流施加到幅材上，由此可以使用多个着色剂着色该纤维网并因此显示出多种颜色和/或折射性质。