公开(公告)号：US5707552A

公开(公告)日：1998-01-13

申请号：US711460

申请日：1996-09-11

申请人： Yoshitane Watanabe ,  Keitaro Suzuki ,  Yoshinari Koyama

发明人： Yoshitane Watanabe ,  Keitaro Suzuki ,  Yoshinari Koyama

IPC分类号： C01G30/02 ,  C08K3/22 ,  C09D5/00 ,  C09K3/16 ,  C09K21/02 ,  H01B1/08 ,  B01J13/00 ,  C01G9/00 ,  C09K29/00

CPC分类号： B82Y30/00 ,  C01G30/02 ,  C08K3/2279 ,  C09K21/02 ,  C09K3/16 ,  H01B1/08 ,  C01P2002/72 ,  C01P2002/88 ,  C01P2004/03 ,  C01P2004/04 ,  C01P2004/10 ,  C01P2004/50 ,  C01P2004/61 ,  C01P2004/62 ,  C01P2004/64 ,  C01P2006/12 ,  C01P2006/22 ,  C01P2006/40 ,  C01P2006/60 ,  C01P2006/82

摘要： The object of the invention is to provide a zinc antimonate anhydride and a production method thereof. The invention relates to a particle having a ZnO/Sb.sub.2 O.sub.5 molar ratio in a range of from 0.8 to 1.2, a crystal structure of zinc antimonate anhydride (Znsb.sub.2 O.sub.6), and a primary particle size in a range of from 5 to 500 nm. The production method of these particles comprises the steps of mixing a zinc compound with a colloidal antimony oxide at a ZnO/Sb.sub.2 O.sub.5 molar rate in a range of from 0.8 to 1.2, followed by calcining the mixture within a temperature range of from 500.degree. to 680.degree. C. The particles of this invention are applicable as a flame retardant for plastics, a smoke suppressant, antistatic agent for plastics and glasses, and resistor.

摘要翻译： 本发明的目的是提供一种锑酸锌及其制备方法。 本发明涉及ZnO / Sb2O5摩尔比为0.8〜1.2，锑酸锌（ZnSb2O6）的晶体结构，一次粒径为5〜500nm的粒子。 这些颗粒的制造方法包括以0.5〜1.2的ZnO / Sb 2 O 5摩尔比混合锌化合物与胶态氧化锑的步骤，然后在500〜680℃的温度范围内煅烧 本发明的颗粒可用作塑料阻燃剂，防烟剂，塑料和玻璃的抗静电剂和电阻剂。

公开(公告)号：US5766512A

公开(公告)日：1998-06-16

申请号：US759887

申请日：1996-12-03

申请人： Yoshitane Watanabe ,  Keitaro Suzuki ,  Yoshinari Koyama

发明人： Yoshitane Watanabe ,  Keitaro Suzuki ,  Yoshinari Koyama

IPC分类号： C01G30/02 ,  C09K3/16 ,  H01B1/08 ,  B01J13/00 ,  C01G9/00 ,  C09K29/00

CPC分类号： B82Y30/00 ,  C01G30/02 ,  C09K3/16 ,  H01B1/08 ,  C01P2002/72 ,  C01P2004/04 ,  C01P2004/10 ,  C01P2004/62 ,  C01P2004/64 ,  C01P2006/12 ,  C01P2006/22 ,  C01P2006/40 ,  C01P2006/60 ,  C01P2006/82

摘要： The object of the invention is to provide a zinc antimonate anhydride and a production method thereof. The invention relates to a particle having a ZnO/Sb.sub.2 O.sub.5 molar ratio in a range of from 0.8 to 1.2, a crystal structure of zinc antimonate anhydride (Znsb.sub.2 O.sub.6), and a primary particle size in a range of from 5 to 500 nm. The production method of these particles comprises the steps of mixing a zinc compound with a colloidal antimony oxide at a ZnO/Sb.sub.2 O.sub.5 molar rate in a range of from 0.8 to 1.2, followed by calcining the mixture within a temperature range of from 500.degree. to 1100.degree. C. The particles of this invention are applicable as a flame retardant for plastics, a smoke suppressant, antistatic agent for plastics and glasses, and resistor.

摘要翻译： 本发明的目的是提供一种锑酸锌及其制备方法。 本发明涉及ZnO / Sb2O5摩尔比为0.8〜1.2，锑酸锌（ZnSb2O6）的晶体结构，一次粒径为5〜500nm的粒子。 这些颗粒的制造方法包括以0.5〜1.2的ZnO / Sb 2 O 5摩尔比混合锌化合物和胶体氧化锑的步骤，然后在500〜1100℃的温度范围内煅烧该混合物 本发明的颗粒可用作塑料阻燃剂，防烟剂，塑料和玻璃的抗静电剂和电阻剂。