摘要:
The use of polyelectrolyte complexes is described, for providing an oxygen barrier to packaging materials made of polymer foils. Polymeric components of the polyelectrolyte complex are applied in polymerized form to the polymer foil. The polymer foil is either coated with an aqueous dispersion comprising a dispersed polyelectrolyte complex previously produced by water-in-water emulsion polymerization, or is coated with a composition comprising a polyelectrolyte complex produced from anionic polymer and from cationic surfactant, or the polymer foil is coated with at least three alternating layers, where respectively one of two adjacent layers comprises an anionic polyelectrolyte component and the other of two adjacent layers comprises a cationic polyelectrolyte component, and polyelectrolyte complexes form at the opposite, adjacent interfaces of the alternating layers.
摘要:
The use of polyelectrolyte complexes is described, for providing an oxygen barrier to packaging materials made of polymer foils. Polymeric components of the polyelectrolyte complex are applied in polymerized form to the polymer foil. The polymer foil is either coated with an aqueous dispersion comprising a dispersed polyelectrolyte complex previously produced by water-in-water emulsion polymerization, or is coated with a composition comprising a polyelectrolyte complex produced from anionic polymer and from cationic surfactant, or the polymer foil is coated with at least three alternating layers, where respectively one of two adjacent layers comprises an anionic polyelectrolyte component and the other of two adjacent layers comprises a cationic polyelectrolyte component, and polyelectrolyte complexes form at the opposite, adjacent interfaces of the alternating layers.
摘要:
A description is given of a method of producing packaging, the packaging surface being coated with a polyelectrolyte complex, and the polyelectrolyte complex being composed of at least one first polymer and at least one second polymer, the first polymer being an anionic polymer and the second polymer being a cationic polymer. The packaging is distinguished by good fat barrier properties.
摘要:
A description is given of a method of producing packaging, the packaging surface being coated with a polyelectrolyte complex, and the polyelectrolyte complex being composed of at least one first polymer and at least one second polymer, the first polymer being an anionic polymer and the second polymer being a cationic polymer. The packaging is distinguished by good fat barrier properties.
摘要:
The use of polyelectrolyte complexes as plasticizer barrier is described, in particular those formed from anionic polymer and from cationic polymer, as also are plasticized substrates and production of the same, where the plasticized substrates have been coated with at least one layer which comprises at least one polyelectrolyte complex.
摘要:
Described is a recloseable pack having a cold-sealed layer of adhesive which is recloseable after the pack has been opened, the layer of adhesive comprising an emulsion polymer composed to an extent of at least 60% by weight of principal monomers selected from the group consisting of C1 to C20 alkyl (meth)acrylates, vinyl esters of carboxylic acids comprising up to 20 C atoms, vinylaromatics having up to 20 C atoms, ethylenically unsaturated nitriles, vinyl halides, vinyl ethers of alcohols comprising 1 to 10 C atoms, aliphatic hydrocarbons having 2 to 8 C atoms and one or two double bonds, and mixtures of these monomers, the emulsion polymer being preparable by emulsion polymerization of free-radically polymerizable monomers in the presence of at least one protective colloid. Also described are aqueous polymer dispersions suitable for producing the pack of the invention, and polymer films coated with the polymer dispersions.
摘要:
Described is a recloseable pack having a cold-sealed layer of adhesive which is recloseable after the pack has been opened, the layer of adhesive comprising an emulsion polymer composed to an extent of at least 60% by weight of principal monomers selected from the group consisting of C1 to C20 alkyl (meth)acrylates, vinyl esters of carboxylic acids comprising up to 20 C atoms, vinylaromatics having up to 20 C atoms, ethylenically unsaturated nitriles, vinyl halides, vinyl ethers of alcohols comprising 1 to 10 C atoms, aliphatic hydrocarbons having 2 to 8 C atoms and one or two double bonds, and mixtures of these monomers, the emulsion polymer being preparable by emulsion polymerization of free-radically polymerizable monomers in the presence of at least one protective colloid. Also described are aqueous polymer dispersions suitable for producing the pack of the invention, and polymer films coated with the polymer dispersions.
摘要:
Described is the use of a microwave-activatable adhesive composition for producing folding-carton blanks for the microwave-activated production of folding cartons. The adhesive composition preferably at less than or equal to 25° C. has an Ig G′ value of greater than or equal to 6 and at greater than or equal to 120° C. has an Ig G′ value of less than or equal to 4, and comprises at least one polymer having a glass transition temperature of greater than 30° C., the folding-carton blanks with adhesive composition applied thereto being blocking-resistant at 25° C. prior to microwave activation.
摘要:
Adhesives comprising: a) from 5.0 to 95.0% by weight of an adhesive dispersion having a viscosity in the range from 2000 to 10,000 mpPa·s, which comprises (a1) an aqueous polymer dispersion which is obtainable by free-radical polymerization of a mixture M which comprises at least one ethylenically unsaturated monomer A to give a polymer P in the presence of at least one protective colloid-based on a water-soluble prepolymer which comprises at least one water-soluble monomer B, and further additives if desired, (a2) if desired, a base selected from the group consisting of alkali metal.hydroxides, ammonia and volatile organic amines, (a3) if desired, a completely water-miscible organic solvent, and, further additives; (b) from 0 to 90.0% by weight of a polysaccharide and/or a protein and/or a protein degradation product; (c) from 0 to 95.0% by weight of at least one filler; (d) from 0 to 10.0% by weight of at least one emulsifier; (e) from 0 to 30.0% by weight of further additives; (f) water to 100% by weight; processes for their preparation, and their use.
摘要:
An adhesive film which comprises at least two continuous polymer phases A and B each formed from a polymer or polymer mixture A (polymer A for short) and a polymer or polymer mixture B (polymer B for short) and which is obtainable by filming at least one of the polymers, A or B, initially in the form of an aqueous polymer dispersion.