公开(公告)号：US20100028659A1

公开(公告)日：2010-02-04

申请号：US12311525

申请日：2007-10-02

申请人： Kazuhisa Shimono ,  Tatsuo Takano ,  Toru Kawazu

发明人： Kazuhisa Shimono ,  Tatsuo Takano ,  Toru Kawazu

IPC分类号： B32B5/16 ,  C09D1/00 ,  C09D189/00 ,  C09D103/02 ,  C09D109/08

CPC分类号： C01F11/181 ,  C01P2004/10 ,  C01P2004/61 ,  C08K3/26 ,  C09D7/61 ,  C09D7/68 ,  C09D7/69 ,  D21H19/385 ,  D21H21/52 ,  Y10T428/258

摘要： A coating solution comprising: (A) an aragonite-type light calcium carbonate microparticle having an average major axis diameter of 1.0 to 2.8 μm and an average minor axis diameter of 0.15 to 0.3 μm, which is produced by diluting a calcium hydroxide slurry that has been treated by high-speed shearing until the slurry has a viscosity of 1000 cP or more at a concentration of 400 g/l to a concentration more than 50 g/l and then blowing carbon dioxide into the diluted slurry at a reaction starting temperature of 20 to 60° C. and at a rate of 1 to 3 l/min per kg of calcium hydroxide; and (B) a pigment comprising a wet heavy calcium carbonate cake. The coating solution enables to provide a coated paper having an excellent degree of brilliance and an excellent degree of whiteness, despite containing no kaolin.

摘要翻译： 一种涂布溶液，其包含：（A）平均长径为1.0〜2.8μm，平均短轴直径为0.15〜0.3μm的文石型轻质碳酸钙微粒，其通过稀释氢氧化钙浆料 通过高速剪切处理直到浆料的粘度为1000cP以上，浓度为400g / l至浓度大于50g / l，然后在二氧化碳的反应开始温度 20至60℃，以每升氢氧化钙1至3升/分钟的速率; 和（B）包含湿重质碳酸钙饼的颜料。 尽管不含高岭土，但是涂布溶液能够提供具有优异的光泽度和优异的白度的涂布纸。

公开(公告)号：US08252413B2

公开(公告)日：2012-08-28

申请号：US12513122

申请日：2007-11-28

申请人： Kazuhisa Shimono ,  Tatsuo Takano ,  Toru Kawazu

发明人： Kazuhisa Shimono ,  Tatsuo Takano ,  Toru Kawazu

IPC分类号： B32B5/16

CPC分类号： C01F11/181 ,  C01F11/18 ,  C01P2004/50 ,  C01P2004/61 ,  C01P2004/62 ,  C01P2006/12 ,  C01P2006/14 ,  C01P2006/16 ,  C01P2006/17 ,  C01P2006/19 ,  D21H17/67 ,  D21H17/675 ,  Y10T428/258 ,  Y10T428/2982

摘要： The light calcium carbonate in the form of microparticle aggregate of the present invention has a BET specific surface area not smaller than 10 m2/g and not larger than 25 m2/g, a pore volume of 0.05 cm3/g or larger for pores having a pore diameter of 0 to 1000 Å as determined by the nitrogen adsorption method, and a pore volume ratio of 25% or more for pores having a pore diameter of 250 Å or smaller based on the total pore volume as determined by the nitrogen adsorption method, and shows an oil absorption of 100 cc/100 g or more as determined by using liquid paraffin. By using this light calcium carbonate as a filler of printing paper, superior ink absorbing property and opacity (especially opacity after printing) can be imparted to the printing paper.

摘要翻译： 本发明的微粒聚集体形式的轻质碳酸钙的BET比表面积不小于10m 2 / g且不大于25m 2 / g，孔体积为0.05cm 3 / g以上 通过氮吸附法测定的孔径为0〜1000，并且通过氮吸附法测定的孔径为250以下的孔的孔体积比为25％以上， 并且显示出通过使用液体石蜡测定的100cc / 100g或更多的吸油量。 通过使用这种轻质碳酸钙作为印刷纸的填料，可以赋予印刷纸更好的吸墨性和不透明性（特别是印刷后的不透明度）。

公开(公告)号：US08017101B2

公开(公告)日：2011-09-13

申请号：US10556934

申请日：2004-06-03

申请人： Kazuo Yamashita ,  Kazuhisa Shimono ,  Toru Kawazu ,  Tatsuo Takano

发明人： Kazuo Yamashita ,  Kazuhisa Shimono ,  Toru Kawazu ,  Tatsuo Takano

IPC分类号： C01F11/18 ,  C09C1/02

CPC分类号： D21H17/675 ,  C01F11/181 ,  C01P2004/10 ,  C01P2004/50 ,  C01P2004/54 ,  C01P2004/61 ,  C01P2004/62 ,  C01P2006/12 ,  C01P2006/14

摘要： Carbon dioxide containing gas is blown into a calcium hydroxide slurry having a calcium hydroxide concentration of 100 to 400 g/L obtained by wet slaking calcined lime with 4 N hydrochloric acid activity (value at 3 minutes) of 150 to 400 mL to allow them to react until the carbonation rate becomes 50 to 85%, then 1 to 20% by volume of the calcium hydroxide slurry is added, and carbon dioxide containing gas is further blown in to terminate the reaction. The calcium carbonate obtained by this method is precipitated calcium carbonate aggregates having a secondary particle diameter of 1 to 10 μm and consisting of primary particles having a long diameter of 0.5 to 3.0 μm, a short diameter of 0.1 to 1.0 μm and an aspect ratio of 3 or more, has superior characteristics due to a BET specific surface area in the range of 8 to 20 m2/g and a pore volume in the range of 1.5 to 3.5 cm3/g, can be uniformly dispersed in pulp fiber, and thereby can be used to manufacture high bulk paper.

摘要翻译： 将含二氧化碳的气体吹入氢氧化钙浆料中，氢氧化钙浆料的氢氧化钙浓度为100〜400g / L，通过湿法煅烧石灰，4N盐酸活性（3分钟的值）为150〜400mL， 反应直到碳酸化速率达到50〜85％，然后加入1〜20体积％的氢氧化钙浆料，并进一步吹入含二氧化碳的气体以终止反应。 通过该方法得到的碳酸钙是二次粒径为1〜10μm的沉淀碳酸钙聚集体，其长径为0.5〜3.0μm，短径为0.1〜1.0μm，长径比为 3以上，由于比表面积为8〜20m 2 / g，孔体积为1.5〜3.5cm 3 / g，能够均匀地分散在纸浆纤维中，因此可以 用于制造高散纸。

公开(公告)号：US20100068506A1

公开(公告)日：2010-03-18

申请号：US12513122

申请日：2007-11-28

申请人： Kazuhisa Shimono ,  Tatsuo Takano ,  Toru Kawazu

发明人： Kazuhisa Shimono ,  Tatsuo Takano ,  Toru Kawazu

IPC分类号： B32B5/16 ,  C01F11/18

CPC分类号： C01F11/181 ,  C01F11/18 ,  C01P2004/50 ,  C01P2004/61 ,  C01P2004/62 ,  C01P2006/12 ,  C01P2006/14 ,  C01P2006/16 ,  C01P2006/17 ,  C01P2006/19 ,  D21H17/67 ,  D21H17/675 ,  Y10T428/258 ,  Y10T428/2982

摘要： The light calcium carbonate in the form of microparticle aggregate of the present invention has a BET specific surface area not smaller than 10 m2/g and not larger than 25 m2/g, a pore volume of 0.05 cm3/g or larger for pores having a pore diameter of 0 to 1000 Å as determined by the nitrogen adsorption method, and a pore volume ratio of 25% or more for pores having a pore diameter of 250 Å or smaller based on the total pore volume as determined by the nitrogen adsorption method, and shows an oil absorption of 100 cc/100 g or more as determined by using liquid paraffin. By using this light calcium carbonate as a filler of printing paper, superior ink absorbing property and opacity (especially opacity after printing) can be imparted to the printing paper.

摘要翻译： 本发明的微粒聚集体形式的轻质碳酸钙的BET比表面积不小于10m 2 / g且不大于25m 2 / g，孔体积为0.05cm 3 / g以上 通过氮吸附法测定的孔径为0〜1000，并且通过氮吸附法测定的孔径为250以下的孔的孔体积比为25％以上， 并且显示出通过使用液体石蜡测定的100cc / 100g或更多的吸油量。 通过使用这种轻质碳酸钙作为印刷纸的填料，可以赋予印刷纸更好的吸墨性和不透明性（特别是印刷后的不透明度）。

公开(公告)号：US20070169905A1

公开(公告)日：2007-07-26

申请号：US10556934

申请日：2004-06-03

申请人： Kazuo Yamashita ,  Kazuhisa Shimono ,  Toru Kawazu ,  Tatsuo Takano

发明人： Kazuo Yamashita ,  Kazuhisa Shimono ,  Toru Kawazu ,  Tatsuo Takano

IPC分类号： C09C1/02 ,  C01F11/18 ,  D21H17/67

CPC分类号： D21H17/675 ,  C01F11/181 ,  C01P2004/10 ,  C01P2004/50 ,  C01P2004/54 ,  C01P2004/61 ,  C01P2004/62 ,  C01P2006/12 ,  C01P2006/14

摘要： Carbon dioxide containing gas is blown into a calcium hydroxide slurry having a calcium hydroxide concentration of 100 to 400 g/L obtained by wet slaking calcined lime with 4 N hydrochloric acid activity (value at 3 minutes) of 150 to 400 mL to allow them to react until the carbonation rate becomes 50 to 85%, then 1 to 20% by volume of the calcium hydroxide slurry is added, and carbon dioxide containing gas is further blown in to terminate the reaction. The calcium carbonate obtained by this method is precipitated calcium carbonate aggregates having a secondary particle diameter of 1 to 10 μm and consisting of primary particles having a long diameter of 0.5 to 3.0 μm, a short diameter of 0.1 to 1.0 μm and an aspect ratio of less than 3, has superior characteristics due to a BET specific surface area in the range of 8 to 20 m2/g and a pore volume in the range of 1.5 to 3.5 cm3/g, can be uniformly dispersed in pulp fiber, and thereby can be used to manufacture high bulk paper.

摘要翻译： 将含二氧化碳的气体吹入氢氧化钙浆料中，氢氧化钙浆料的氢氧化钙浓度为100〜400g / L，通过湿法煅烧石灰，4N盐酸活性（3分钟的值）为150〜400mL， 反应直到碳酸化速率达到50〜85％，然后加入1〜20体积％的氢氧化钙浆料，并进一步吹入含二氧化碳的气体以终止反应。 通过该方法得到的碳酸钙是二次粒径为1〜10μm的沉淀碳酸钙凝集体，长径为0.5〜3.0μm的初级粒子，0.1〜1.0μm的短径，长径比为 小于3，由于BET比表面积在8至20m 2 / g的范围内具有优异的特性，并且孔体积在1.5至3.5cm 3 / SUP> / g可以均匀分散在纸浆纤维中，从而可用于制造高质量纸。

公开(公告)号：US5879442A

公开(公告)日：1999-03-09

申请号：US998034

申请日：1997-12-23

申请人： Hiroyuki Nishiguchi ,  Kazuhisa Shimono ,  Tetsuo Kumasaka

发明人： Hiroyuki Nishiguchi ,  Kazuhisa Shimono ,  Tetsuo Kumasaka

IPC分类号： C01F11/18 ,  C09C1/02 ,  D21H19/38 ,  D21H19/54 ,  D21H19/58

CPC分类号： C01F11/185 ,  C09C1/021 ,  D21H19/385 ,  B41M5/5218 ,  C01P2004/61 ,  C01P2004/62 ,  C01P2006/12 ,  C01P2006/22 ,  D21H19/54 ,  D21H19/58

摘要： Proposed is a method for the preparation of an aqueous slurry of calcium carbonate particles suitable as a base pigment in the preparation of a paper coating composition having excellent water retentivity and high solid concentration with good flowability, which contains precipitated and ground calcium carbonate particles in combination in a specified weight proportion and characterized by several parameters. The aqueous slurry is prepared in a process comprising the steps of: (a) subjecting an aqueous slurry or wet cake containing a specified amount of specific precipitated calcium carbonate particles to a primary dispersing treatment using a mixer to a specified extent; (b) admixing the aqueous slurry with a specified amount of specific ground calcium carbonate particles; (c) subjecting the aqueous slurry to a secondary dispersing treatment using a mixer to a specified extent; and (d) subjecting the aqueous slurry to a tertiary dispersing treatment using a sand grinder to a specified extent.

摘要翻译： 提出了一种制备适合作为基础颜料的碳酸钙颗粒的水性浆料的方法，其制备具有优异的保水性和高固体浓度以及良好流动性的纸涂料组合物，其含有沉淀和研磨的碳酸钙颗粒的组合 以指定的重量比例，并用几个参数表征。 含水浆料的制备方法包括以下步骤：（a）使含有特定量的特定沉淀碳酸钙颗粒的含水浆料或湿滤饼在一定程度上进行初步分散处理; （b）将含水浆料与指定量的特定磨碎的碳酸钙颗粒混合; （c）使用混合器对含水浆料进行二次分散处理至一定程度; 和（d）使用砂磨机对含水浆料进行三级分散处理达到规定的程度。