公开(公告)号：US20130105045A1
公开(公告)日：2013-05-02
申请号：US13662132
申请日：2012-10-26
Applicant: Alcoa Inc.
Inventor： Xinyan Yan , Jen C. Lin
Abstract: An aluminum casting alloy has 8.5-9.5 wt. % silicon, 0.5-2.0 wt. % copper (Cu), 0.27-0.53 wt. % magnesium (Mg), wherein the aluminum casting alloy includes copper and magnesium such that 4.7≦(Cu+10Mg)≦5.8, and other elements, the balance being aluminum. Selected elements may be added to the base composition to give resistance to degradation of tensile properties due to exposure to heat. The thermal treatment of the alloy is calculated based upon wt. % composition to solutionize unwanted phases having a negative impact on properties and may include a three level ramp-up and soak to a final temperature followed by cold water quenching and artificial aging.
Abstract translation: 铝铸造合金具有8.5-9.5重量％ ％硅，0.5-2.0重量％ ％铜（Cu），0.27-0.53重量％ ％镁（Mg），其中铝铸造合金包括铜和镁，使得4.7 @（Cu + 10Mg）@ 5.8和其它元素，余量为铝。 可以将选择的元素加入到基础组合物中以使其耐受由于暴露于热而引起的拉伸性能的降解。 合金的热处理基于wt计算。 ％组合物以将不利相的相位溶解以对性质具有负面影响，并且可以包括三级倾斜并浸泡到最终温度，然后进行冷水淬灭和人造老化。
-
2.发明授权公开(公告)号：US09249487B2
公开(公告)日：2016-02-02
申请号：US13827918
申请日：2013-03-14
Applicant: Alcoa Inc.
Inventor： Xinyan Yan , Wenping Zhang , Dana Clark , James Daniel Bryant , Jen Lin
Abstract: New methods for aging aluminum alloys having zinc and magnesium are disclosed. The methods may include first aging the aluminum alloy at a first temperature of from about 330° F. to 530° F. and for a first aging time of from 1 minute to 6 hours, and then second aging the aluminum alloy at a second temperature for a second aging time of at least 30 minutes, with the second temperature being lower than the first temperature.
Abstract translation: 公开了具有锌和镁的老化铝合金的新方法。 所述方法可以包括在约330°F至530°F的第一温度和1分钟至6小时的第一老化时间之前首先老化铝合金，然后在第二温度下对铝合金进行二次老化 第二老化时间至少为30分钟，第二温度低于第一温度。
-
公开(公告)号：US20170016092A1
公开(公告)日：2017-01-19
申请号：US14574933
申请日：2014-12-18
Applicant: ALCOA INC.
Inventor： Xinyan Yan , Jen C. Lin
Abstract: New aluminum casting alloys having 8.5-9.5 wt. % silicon, 0.8-2.0 wt. % copper (Cu), 0.20-0.53 wt. % magnesium (Mg), and 0.35 to 0.8 wt. % manganese are disclosed. The alloy may be solution heat treated, treated in accordance with T5 tempering and/or artificially aged to produce castings, e.g., for cylinder heads and engine blocks. In one embodiment, the castings are made by high pressure die casting.
Abstract translation: 具有8.5-9.5重量％ ％硅，0.8-2.0重量％ ％铜（Cu），0.20-0.53重量％ ％镁（Mg）和0.35〜0.8重量％ 公开了锰。 该合金可以进行固溶热处理，根据T5回火处理和/或人工老化以生产铸件，例如用于气缸盖和发动机缸体。 在一个实施例中，铸件通过高压压铸制成。
-
4.发明申请公开(公告)号：US20150376754A1
公开(公告)日：2015-12-31
申请号：US13827918
申请日：2013-03-14
Applicant: ALCOA INC.
Inventor： Xinyan Yan , Wenping Zhang , Dana Clark , James Daniel Bryant , Jen Lin
Abstract: New methods for aging aluminum alloys having zinc and magnesium are disclosed. The methods may include first aging the aluminum alloy at a first temperature of from about 330° F. to 530° F. and for a first aging time of from 1 minute to 6 hours, and then second aging the aluminum alloy at a second temperature for a second aging time of at least 30 minutes, with the second temperature being lower than the first temperature.
Abstract translation: 公开了具有锌和镁的老化铝合金的新方法。 所述方法可以包括在约330°F至530°F的第一温度和1分钟至6小时的第一老化时间之前首先老化铝合金，然后在第二温度下对铝合金进行二次老化 第二老化时间至少为30分钟，第二温度低于第一温度。
-
公开(公告)号：US20150315680A1
公开(公告)日：2015-11-05
申请号：US14694109
申请日：2015-04-23
Applicant: ALCOA INC.
Inventor： Xinyan Yan , Eider Simielli , Jen C. Lin , Wenping Zhang , James Daniel Bryant
Abstract: New 7xx aluminum casting alloys are disclosed. The aluminum casting alloys generally include from 3.0 to 8.0 wt. % Zn, from 1.0 to 3.0 wt. % Mg, where the wt. % Zn exceeds the wt. % Mg, from 0.35 to 1.0 wt. % Cu, where the wt. % Mg exceeds the wt. % Cu, from 0.05 to 0.30 wt. % V, from 0.01 to 1.0 wt. % of at least one secondary element (Mn, Cr, Zr, Ti, B, and combinations thereof), up to 0.50 wt. % Fe, and up to 0.25 wt. % Si, the balance being aluminum and other elements, wherein the aluminum casting alloy include not greater than 0.05 wt. % each of the other elements, and wherein the aluminum casting alloy includes not greater than 0.15 wt. % in total of the other elements.
Abstract translation: 公开了新的7xx铝铸造合金。 铝铸造合金通常包括3.0至8.0重量％ ％Zn，1.0〜3.0wt。 ％Mg，其中wt。 ％Zn超过wt。 ％Mg，0.35〜1.0wt。 ％Cu，其中wt。 ％Mg超过wt。 ％Cu，0.05-0.30重量％ ％V，0.01〜1.0wt。 至少一种次要元素（Mn，Cr，Zr，Ti，B及其组合）的％，至多0.50重量％ ％Fe，至多0.25wt。 ％Si，余量为铝和其他元素，其中铝铸造合金包括不大于0.05重量％ ％的其他元素，其中铝铸造合金包括不大于0.15wt。 其他元素总数的百分比。
-
Patent Agency Ranking
公开(公告)号：US10227679B2
公开(公告)日：2019-03-12
申请号：US14574933
申请日：2014-12-18
Applicant: ALCOA INC.
Inventor： Xinyan Yan , Jen C. Lin
Abstract: New aluminum casting alloys having 8.5-9.5 wt. % silicon, 0.8-2.0 wt. % copper (Cu), 0.20-0.53 wt. % magnesium (Mg), and 0.35 to 0.8 wt. % manganese are disclosed. The alloy may be solution heat treated, treated in accordance with T5 tempering and/or artificially aged to produce castings, e.g., for cylinder heads and engine blocks. In one embodiment, the castings are made by high pressure die casting.
-
公开(公告)号：US10174409B2
公开(公告)日：2019-01-08
申请号：US13662132
申请日：2012-10-26
Applicant: ALCOA INC.
Inventor： Xinyan Yan , Jen C. Lin
Abstract: An aluminum casting alloy has 8.5-9.5 wt. % silicon, 0.5-2.0 wt. % copper (Cu), 0.27-0.53 wt. % magnesium (Mg), wherein the aluminum casting alloy includes copper and magnesium such that 4.7≤(Cu+10Mg)≤5.8, and other elements, the balance being aluminum. Selected elements may be added to the base composition to give resistance to degradation of tensile properties due to exposure to heat. The thermal treatment of the alloy is calculated based upon wt. % composition to solutionize unwanted phases having a negative impact on properties and may include a three level ramp-up and soak to a final temperature followed by cold water quenching and artificial aging.
-
公开(公告)号：US20160281195A1
公开(公告)日：2016-09-29
申请号：US15092412
申请日：2016-04-06
Applicant: ALCOA INC.
Inventor： Xinyan Yan , Jen C. Lin
Abstract: An aluminum casting alloy has 8.5-9.5 wt. % silicon, 0.5-2.0 wt. % copper (Cu), 0.27-0.53 wt. % magnesium (Mg), wherein the aluminum casting alloy includes copper and magnesium such that 4.7≦(Cu+10Mg)≦5.8, and other elements, the balance being aluminum. Selected elements may be added to the base composition to give resistance to degradation of tensile properties due to exposure to heat. The thermal treatment of the alloy is calculated based upon wt. % composition to solutionize unwanted phases having a negative impact on properties and may include a three level ramp-up and soak to a final temperature followed by cold water quenching and artificial aging.
Abstract translation: 铝铸造合金具有8.5-9.5重量％ ％硅，0.5-2.0重量％ ％铜（Cu），0.27-0.53重量％ ％镁（Mg），其中铝铸造合金包括铜和镁，使得4.7≤（Cu + 10Mg）≤5.8，其余元素为铝。 可以将选择的元素加入到基础组合物中以使其耐受由于暴露于热而引起的拉伸性能的降解。 合金的热处理基于wt计算。 ％组合物以将不利相的相位溶解以对性质具有负面影响，并且可以包括三级倾斜并浸泡到最终温度，然后进行冷水淬灭和人造老化。
-
9.发明申请公开(公告)号：US20150259774A1
公开(公告)日：2015-09-17
申请号：US14206448
申请日：2014-03-12
Applicant: ALCOA INC.
Inventor： Xinyan Yan , Wenping Zhang , Dana Clark , James Daniel Bryant , Jen Lin
Abstract: New methods for aging aluminum alloys having zinc and magnesium are disclosed. The methods may include first aging the aluminum alloy at a first temperature of from about 310° F. to 530° F. and for a first aging time of from 1 minute to 6 hours, and then second aging the aluminum alloy at a second temperature for a second aging time of at least 30 minutes, with the second temperature being lower than the first temperature.
Abstract translation: 公开了具有锌和镁的老化铝合金的新方法。 所述方法可以包括在约310°F至530°F的第一温度和1分钟至6小时的第一老化时间之前对铝合金进行老化，然后在第二温度下对铝合金进行二次老化 第二老化时间至少为30分钟，第二温度低于第一温度。
-
10.发明申请公开(公告)号：US20150122660A1
公开(公告)日：2015-05-07
申请号：US14592297
申请日：2015-01-08
Applicant: ALCOA INC.
Inventor： Jen C. Lin , James R. Fields , Albert L. Askin , Xinyan Yan , Ralph R. Sawtell , Shawn Patrick Sullivan , Janell Lyn Abbott
CPC classification number: C25D11/16 , B22D17/00 , B22D17/20 , B22D21/007 , B22D25/00 , C22C21/00 , C25D5/02 , C25D9/06 , C25D11/022 , C25D11/04 , C25D11/18 , Y10T428/12736 , Y10T428/26
Abstract: Decorative shape cast products and methods, systems, compositions and apparatus for producing the same are described. In one embodiment, the decorative shape cast products are produced from an Al—Ni or Al—Ni—Mn alloy, with a tailored microstructure to facilitate production of anodized decorative shape cast product having the appropriate finish and mechanical properties.
Abstract translation: 描述了用于制造它们的装饰造型产品和方法，系统，组合物和装置。 在一个实施例中，装饰形状铸造产品由Al-Ni或Al-Ni-Mn合金制成，具有定制的微观结构，以便于生产具有适当精加工和机械性能的阳极氧化装饰性铸造产品。
-
-
-
-
-
-
-
-
-