摘要:
Provided is a method for producing a polyarylene sulfide resin, the method including subjecting a dihaloaromatic compound and a sulfidizing agent to a polymerization reaction in the presence of an aliphatic cyclic compound having a ring openable by hydrolysis, in which corrosion of a production apparatus is suppressed. More particularly, provided is a method for producing a polyarylene sulfide resin, the method including a dehydration step (1) in which a water-containing sulfidizing agent and an aliphatic cyclic compound having a ring openable by hydrolysis are heated in the presence of a dihaloaromatic compound to a liquid temperature in the range of 90° C. or higher and 170° C. or lower under the atmospheric pressure, and then dehydration is performed while maintaining the liquid temperature and reducing the pressure to a pressure in the range of 30 [kPa abs] or higher and 80 [kPa abs] or lower to thus obtain a mixture.
摘要:
The present application relates to a method for extracting coenzyme Q10 and a phospholipid from a coenzyme Q10 fermentation bacterium powder. The method is characterized in that the fermentation bacterium powder of a coenzyme Q10 production strain is subjected to extraction with a mixed solvent of which the three-dimensional Hansen solubility parameter is between 21 and 23 (J/cm3)1/2 and the hydrogen bonding solubility parameter thereof is between 10 and 12 (J/cm3)1/2. The present invention can efficiently extract two products, namely coenzyme Q10 and a phospholipid, from the coenzyme Q10 fermentation bacterium powder; the process thereof is highly operable, easy to be industrialized, and can provide a product with high purity and yield, having great economic benefit.
摘要:
To provide a method for producing granular polyarylene sulfide (hereinafter, PAS), the method capable of providing granular PAS having high particle strength and low melt viscosity in high yield without using special additives and the like; and granular PAS.A method according to the present invention is a method for producing granular PAS having a melt viscosity of from 1 to 30 Pa.s, which is measured at a temperature of 310° C. and a shear rate of 1216/s, by polymerizing a sulfur source and a dihalo aromatic compound in an organic amide solvent.
摘要:
The present invention provides a production method and a production apparatus for a polyarylene sulfide (PAS), thus the formation of a floating polymer and the leakage of the floating polymer to the outside of the vessel in a washing step are prevented, to achieve steady production of the polymer with high quality, to improve the yield of the polymer and to reduce environmental load, wherein the floating polymer refers to a particles of the polymer which are floating on the surface of a washing solution, in the upper part of the inside of a washing vessel, as a result of the adhesion of a gas onto the surface of the particles of the polymer.The present invention provides a production method for a PAS comprising step (I), performing polymerization, step (II), separating and collecting a polymer, step (III), washing a slurry, and step (IV), collecting the polymer after washing, wherein an aqueous medium is sprayed onto a PAS floating on the surface of the aqueous washing solution in the upper part of the inside of the washing vessel in step (III) (step (IIIa), washing a slurry using a counter current, and/or step (IIIb), treating a slurry with acid using a counter current, or the like); and a production apparatus for a PAS comprising a washing device (counter current washing device and/or a counter current contact/acid treatment device or the like) having an aqueous medium spray means.
摘要:
A poly(phenylene sulfide) fiber contains 1-10% by weight of a poly(phenylene sulfide) oligomer having a weight-average molecular weight of 5,000 or less, has a difference between a cold crystallization heat quantity (ΔHc) and a crystal melting heat quantity (ΔHm) during temperature rising in DSC, ΔHm−ΔHc, of 25 J/g or larger, and has an elongation of less than 40% and a strength of 3.0 cN/dtex or higher. The poly(phenylene sulfide) fiber has high heat resistance and chemical resistance and high strength and, despite this, has excellent suitability for high-order processing, e.g., thermal shapability, because the amorphous parts thereof have high molecular movability.
摘要:
The invention relates to polyarylene sulphides with melt viscosities settable to defined values. The products are distinguished by high stability of the melt. They are obtained by adding, in the preparation of these polyarylene sulphides, certain phenols as chain terminators to the reaction mixture.
摘要:
This invention relates to a process for the preparation of high molecular weight, optionally branched polyarylene sulphides. These may be prepared in polar organic solvents in the absence of water, substances containing water being dehydrated in the reaction mixture before the reaction.
摘要:
This invention relates to a process for the production of high molecular weight, optionally branched polyarylene sulphides. These polyarylene sulphides may be produced in a polar organic solvent in the absence of water in a one-vessel reaction.
摘要:
A polyphenylene sulfide resin composition for automotive cooling parts contains, with respect to 100 parts by weight of a polyphenylene sulfide resin (A): 30 to 110 parts by weight of glass fibers (B); and 0.1 to 3 parts by weight of a silane compound (C) having a functional group selected from an amino group and an isocyanate group. In this polyphenylene sulfide resin composition, the PPS resin (A) has a number-average molecular weight of 7,000 to 14,000, and gives a residue amount of 2.0 to 5.0% by weight when dissolved in 20-fold amount by weight of 1-chloronaphthalene at 250° C. for 5 minutes and subsequently subjected to heat pressure filtration through a PTFE membrane filter having a pore size of 1 μm.
摘要:
The present disclosure relates to a method of more efficiently separating and purifying a polyarylene sulfide exhibiting excellent strength, heat resistance, flame retardancy, and processability when processed into a molded product after polymerization.