公开(公告)号：US06723265B1

公开(公告)日：2004-04-20

申请号：US09889454

申请日：2001-07-17

申请人： Hiroyuki Osaka ,  Satoshi Nagamune ,  Kenji Iwashita

发明人： Hiroyuki Osaka ,  Satoshi Nagamune ,  Kenji Iwashita

IPC分类号： D01D5088

CPC分类号： D01D5/082 ,  D01F6/62 ,  D02G1/0206 ,  D02G1/18

摘要： A polymer of a kind different from a polyester in an amount within the range of 0.3 to 5.0% by weight based on the polyester is added to the polyester, and the resulting composition is melt-extruded from the same pack. The extruded filament group including polyester multi-filaments is cooled once to the glass transition temperature or below, and the filament group is subsequently divided into two groups. One of the filament groups in an opened state is subjected to non-contact heat treatment at an atmospheric temperature of 120° C. or above; however, the other filament group is kept in a state without being subjected to the heat treatment. The respective filament groups are then simultaneously taken off at a speed of 2500 m/min or above and subjected to doubling and mixing of the filaments.

摘要翻译： 在聚酯中加入与聚酯不同的聚合物，其量为0.3-5.0重量％，并将所得组合物从同一包装熔体挤出。 将包含聚酯多丝的挤出长丝组冷却至玻璃化转变温度以下，然后将丝束分成两组。 处于打开状态的丝线组之一在120℃或更高的大气温度下进行非接触热处理; 然而，另一个长丝组保持在不经受热处理的状态。 然后，以2500m /分钟以上的速度同时取出各个长丝组，并进行长丝加倍混合。

公开(公告)号：US20050227066A1

公开(公告)日：2005-10-13

申请号：US10505525

申请日：2003-04-25

申请人： Masahiro Konishi ,  Satoshi Nagamune ,  Hiroyuki Osaka

发明人： Masahiro Konishi ,  Satoshi Nagamune ,  Hiroyuki Osaka

IPC分类号： D01F6/62 ,  D02G1/02 ,  D02G1/20 ,  B29C47/00 ,  B28B3/20 ,  D02G3/00

CPC分类号： D02G1/02 ,  D01F6/62 ,  D02G1/0266 ,  D02G1/20 ,  Y10T428/29 ,  Y10T428/2913 ,  Y10T428/2967

摘要： There are provided a process for producing a polyester fine multifilament yarn having a single filament fineness of 0.9 dtex or below, a total number of single filaments of 100 to 400 and a birefringence of 0.03 to 0.06 comprising passing polymer streams of a polyester polymer melt extruded from a spinneret surface through an atmosphere wherein a distance of 0 to 40 mm from the spinneret surface is regulated to a temperature within the range of 100 to 300° C., further cooling the polymer streams and then converging the cooled filaments into a filament bundle at a position of 350 to 500 mm from the spinneret surface; a process for producing a polyester fine false twist textured yarn comprising subjecting a polyester fine multifilament yarn having a single filament fineness of 0.9 dtex or below, a total number of single filaments of 100 to 400 and a bifringence of 0.03 to 0.06 to false twist texturing, the process comprising subjecting the multifilament yarn to air interlacing so as to provide a degree of interlacing of 50 to 90 interlaced spots/m measured for the false twist textured yarn, regulating the residence time in a draw-false twisting heater of 0.052 to 0.300 second and the temperature of the running filament yarn at the outlet of the heater to a higher temperature than the glass transition temperature (Tg) of the polyester polymer by 90 to 140° C., subjecting the multifilament yarn to simultaneous draw-false twist texturing at a draw ratio of 1.40 to 1.70 times, providing the false twist textured yarn, applying a finish oil in an amount of 1.3 to 3.0% by weight based on the weight of the false twist textured yarn and winding the resulting yarn under a winding tension of 0.05 to 0.30 cN/dtex at a speed of 500 to 1200 m/min; and a process for producing the polyester fine false twist textured yarn having a single filament fineness of 0.9 dtex or below, a total number of single filaments of 100 and 400 and a birefringence of 0.03 to 0.06 comprising subjecting a polyester multifilament yarn to the simultaneous draw-false twisting and producing the false twist textured yarn, the process comprising the polyester fine multifilament yarn to air interlacing treatment before and after the simultaneous draw-false twist texturing and regulating the degree of interlacing before and after the latter air interlacing treatment to 30 to 60 interlaced spots/m and 70 to 110 interlaced spots/m, respectively.

公开(公告)号：US07078096B2

公开(公告)日：2006-07-18

申请号：US10505525

申请日：2003-04-25

申请人： Masahiro Konishi ,  Satoshi Nagamune ,  Hiroyuki Osaka

发明人： Masahiro Konishi ,  Satoshi Nagamune ,  Hiroyuki Osaka

IPC分类号： D01F6/00

CPC分类号： D02G1/02 ,  D01F6/62 ,  D02G1/0266 ,  D02G1/20 ,  Y10T428/29 ,  Y10T428/2913 ,  Y10T428/2967

摘要： There are provided a process for producing a polyester fine multifilament yarn having a single filament fineness of 0.9 dtex or below, a total number of single filaments of 100 to 400 and a birefringence of 0.03 to 0.06 comprising passing polymer streams of a polyester polymer melt extruded from a spinneret surface through an atmosphere wherein a distance of 0 to 40 mm from the spinneret surface is regulated to a temperature within the range of 100 to 300° C., further cooling the polymer streams and then converging the cooled filaments into a filament bundle at a position of 350 to 500 mm from the spinneret surface; a process for producing a polyester fine false twist textured yarn comprising subjecting a polyester fine multifilament yarn having a single filament fineness of 0.9 dtex or below, a total number of single filaments of 100 to 400 and a bifringence of 0.03 to 0.06 to false twist texturing, the process comprising subjecting the multifilament yarn to air interlacing so as to provide a degree of interlacing of 50 to 90 interlaced spots/m measured for the false twist textured yarn, regulating the residence time in a draw-false twisting heater of 0.052 to 0.300 second and the temperature of the running filament yarn at the outlet of the heater to a higher temperature than the glass transition temperature (Tg) of the polyester polymer by 90 to 140° C., subjecting the multifilament yarn to simultaneous draw-false twist texturing at a draw ratio of 1.40 to 1.70 times, providing the false twist textured yarn, applying a finish oil in an amount of 1.3 to 3.0% by weight based on the weight of the false twist textured yarn and winding the resulting yarn under a winding tension of 0.05 to 0.30 cN/dtex at a speed of 500 to 1200 m/min; and a process for producing the polyester fine false twist textured yarn having a single filament fineness of 0.9 dtex or below, a total number of single filaments of 100 and 400 and a birefringence of 0.03 to 0.06 comprising subjecting a polyester multifilament yarn to the simultaneous draw-false twisting and producing the false twist textured yarn, the process comprising the polyester fine multifilament yarn to air interlacing treatment before and after the simultaneous draw-false twist texturing and regulating the degree of interlacing before and after the latter air interlacing treatment to 30 to 60 interlaced spots/m and 70 to 110 interlaced spots/m, respectively.

公开(公告)号：US07846544B2

公开(公告)日：2010-12-07

申请号：US11793251

申请日：2006-07-05

申请人： Satoshi Nagamune

发明人： Satoshi Nagamune

IPC分类号： B32B27/36 ,  B32B27/02

CPC分类号： D01D5/34 ,  D01F8/14 ,  Y10T428/2929 ,  Y10T428/2931 ,  Y10T428/2933 ,  Y10T428/2938 ,  Y10T428/2969

摘要： [PROBLEMS] To provide a polyester monofilament which shows a high dimensional stability and excellent effects of preventing peel-off in filaments, preventing pirn barre and preventing halation and has a high fineness, a high strength and a high modulus. [MEANS FOR SOLVING PROBLEMS] A core-shell type composite polyester monofilament comprising polyethylene terephthalate at a ratio of 80% by mol or higher, which satisfies the following requirements A to F: A) the intrinsic viscosity of the core component being 0.70 or above and the intrinsic viscosity of the shell component being from 0.55 to 0.60; B) the core component amounting to 50 to 70%; C) at least the shell component containing from 0.2 to 0.4% by weight of metal microparticles; D) the fineness of the monofilament being from 5 to 15 dtex, its modulus at elongation of 5% being from 3 to 4.5 cN/dtex and its elongation at break being from 20 to 40%; E) the free shrinkage of the innermost part under specific conditions being 0.3% or less; and F) the node density is one per 100,000 m or less.

摘要翻译： 本发明提供一种具有高尺寸稳定性和优异的防止细丝剥落的效果的聚酯单丝，防止皮条破坏，防止晕倒，细度高，强度高，模量高。 解决问题的手段以包含聚对苯二甲酸乙二醇酯的比例为80摩尔％以上的芯壳型复合聚酯单丝满足以下要求A〜F：A）核成分的特性粘度为0.70以上 壳组分的特性粘度为0.55至0.60; B）核心部件达50％至70％; C）至少含有0.2至0.4重量％的金属微粒的壳组分; D）单丝的纤度为5〜15dtex，伸长率为5％时的模量为3〜4.5cN / dtex，断裂伸长率为20〜40％。 E）特定条件下最内部的自由收缩率为0.3％以下; 和F）节点密度是每100,000米或更少一个。

公开(公告)号：US20090324948A1

公开(公告)日：2009-12-31

申请号：US11793251

申请日：2006-07-05

申请人： Satoshi Nagamune

发明人： Satoshi Nagamune

IPC分类号： D02G3/00 ,  D01D5/34

CPC分类号： D01D5/34 ,  D01F8/14 ,  Y10T428/2929 ,  Y10T428/2931 ,  Y10T428/2933 ,  Y10T428/2938 ,  Y10T428/2969

摘要： [PROBLEMS] To provide a polyester monofilament which shows a high dimensional stability and excellent effects of preventing peel-off in filaments, preventing pirn barre and preventing halation and has a high fineness, a high strength and a high modulus. [MEANS FOR SOLVING PROBLEMS] A core-shell type composite polyester monofilament comprising polyethylene terephthalate at a ratio of 80% by mol or higher, which satisfies the following requirements A to F: A) the intrinsic viscosity of the core component being 0.70 or above and the intrinsic viscosity of the shell component being from 0.55 to 0.60; B) the core component amounting to 50 to 70%; C) at least the shell component containing from 0.2 to 0.4% by weight of metal microparticles; D) the fineness of the monofilament being from 5 to 15 dtex, its modulus at elongation of 5% being from 3 to 4.5 cN/dtex and its elongation at break being from 20 to 40%; E) the free shrinkage of the innermost part under specific conditions being 0.3% or less; and F) the node density is one per 100,000 m or less.

摘要翻译： 本发明提供一种具有高尺寸稳定性和优异的防止细丝剥落的效果的聚酯单丝，防止皮条破坏，防止晕倒，细度高，强度高，模量高。 解决问题的手段以包含聚对苯二甲酸乙二醇酯的比例为80摩尔％以上的芯壳型复合聚酯单丝满足以下要求A〜F：A）核成分的特性粘度为0.70以上 壳组分的特性粘度为0.55至0.60; B）核心部件达50％至70％; C）至少含有0.2至0.4重量％的金属微粒的壳组分; D）单丝的纤度为5〜15dtex，伸长率为5％时的模量为3〜4.5cN / dtex，断裂伸长率为20〜40％。 E）特定条件下最内部的自由收缩率为0.3％以下; 和F）节点密度是每100,000米或更少一个。