摘要： A hard tempered aluminum alloy sheet useful for deep drawing is prepared by a process comprising the steps of hot rolling an ingot of aluminum alloy consisting essentially of 4.0 to 6.0 Mg wt. %, at least one component selected from the group consisting of 0.1 to 0.7 wt. % Mn, 0.01 to 0.05 wt. % Zr, 0.005 to 0.12 wt. % V and up to 0.05 wt. % Ti and the balance aluminum to a sheet not more than 2.5 mm thick, intermediate annealing the hot rolled alloy and final cold rolling the annealed alloy to effect a rolling reduction of less than 85%.In case the finishing temperature of the hot rolling is adjusted to a temperature of 300.degree. to 350.degree. C., the above intermediate annealing can be omitted.

摘要翻译： 用于深拉伸的硬质回火铝合金板通过包括以下步骤的方法制备，所述方法包括以下步骤：将基本上由4.0至6.0重量％ ％，选自0.1至0.7重量％的至少一种组分。 ％Mn，0.01〜0.05重量％ ％Zr，0.005〜0.12重量％ ％V和高达0.05wt。 ％Ti，余量为铝到不超过2.5mm厚的板，中间退火热轧合金，最终冷轧退火合金，以实现小于85％的轧制压下率。 在热轧的终轧温度调节至300〜350℃的温度的情况下，可以省略上述的中间退火。