The method of this invention produces a silicone coated glass fabric which is translucent or transparent as desired and which has a smooth dry surface. The coated glass fabric is useful in producing air-supported and tension-supported roofs for structures such as greenhouses. A glass fabric is first coated with a polydiorganosiloxane, in which the organo radicals are methyl and phenyl radicals in a ratio of from 0.25 to 3.7, in an amount sufficient to impregnate the fibers in the yarns of the fabric, but leaving the interstices of the fabric open. This first layer is then followed by coating with a polydimethylsiloxane elastomer to give a continuous layer, then coating with an elastoplastic organopolysiloxane resin to give a smooth, dry surface on the glass fabric reinforced sheet.