Molten glass is poured on to a bath of molten metal to form a pool of molten glass on the bath, which pool is held back on the bath surface by an elongate member which can be solid, wetted by the glass, extending across the downstream end of the pool. A ribbon of glass is drawn from a forward flow of molten glass beneath the member and the ribbon is rapidly cooled to stabilize its dimensions as it is drawn away from the member. The glass is heated in the region of the member to maintain forwardly flowing glass in that region at a viscosity which is lower than the viscosity of molten glass of the pool upstream of the member but at viscosity at which the glass also wets on to the member. The ribbon is drawn from the lower viscosity, forwardly flowing glass. The method is suitable for the production of flat glass of thickness in the range 0.5 mm to 10 mm; also the production of glass foil of thickness in the range 0.005 mm to 0.5 mm.