The present invention relates to a steel for mold, containing: 0.28 mass %≤C≤0.65 mass %, 0.01 mass %≤Si≤0.30 mass %, 1.5 mass %≤Mn≤3.0 mass %, 0.5 mass %≤Cr≤1.4 mass %, 1.9 mass %≤Mo+W/2≤4.0 mass %, 0.2 mass %≤V≤1.0 mass %, and 0.01≤N≤0.10 mass %, with the balance being Fe and inevitable impurities, in which, in a state after quenching and tempering, the steel has: a (Mo, W) carbide having a diameter of 0.2 μm or less being in an amount of 1.2 mass % or more, a ratio (mass ratio) of the amount of the (Mo, W) carbide to an amount of a Cr carbide being 11 or more, and a hardness change of 15 HRC or less.