A steel member, a hot-rolled steel sheet to be used as a material thereof, and production methods therefor are provided. A steel member contains 0.010% to 0.120% Ti, in which 0.005% or more of Ti is precipitated as a precipitate having a particle size of 20 nm or less in the microstructure. A hot-rolled steel sheet for the steel member contains 0.010% to 0.120% Ti, in which 0.005% or more of Ti is present as dissolved Ti in the microstructure. A method for producing the steel member includes subjecting a hot-rolled steel sheet to forming processing and then performing heat treatment including heating to a temperature of higher than 550° C. and 1,050° C. or lower and then cooling at an average cooling rate of 10° C./s or more in the temperature range of 550° C. to 400° C.