The invention discloses a hot rolling method for overcoming the landscape stripe chromatic aberration defect of a low-carbon low-silicon hot-rolled acid pickling plate. The hot rolling method comprises the processes of hot rolling, rough rolling and fine rolling. In the rough rolling process, the outlet temperature is 1,080 DEG C or above, and in the fine rolling process, the inlet temperature isnot higher than 1,030 DEG C. According to the method, the outlet temperature of the rough rolling tail pass is increased to be 1,080 DEG C or above, the situations of residual scale crack happening and protruding ridge forming due to base metal extrusion are avoided, the problem about landscape stripes is effectively solved, and the obtained product has the characteristic of good surface quality.Meanwhile, according to the method, an intermediate blank is subjected to water cooling on a roller bed between rough rolling and fine rolling, the requirements of the low-carbon low-silicon hot-rolled acid pickling plate for low-temperature fine rolling can be met, and other scale defects caused by high-temperature fine rolling are overcome. When the method is adopted for producing the low-carbonlow-silicon hot-rolled acid pickling plate, the heating furnace technology the same with that of ordinary low-carbon cold-rolled steel can be adopted, and productivity losses caused in the heating furnace cooling process are avoided.