The invention provides an eliminating method for a brittle phase in a laser-repaired nickel-base high temperature alloy, and belongs to the technical field of metal material heat treatment. The eliminating method comprises the steps that the laser-repaired nickel-base high temperature alloy is sequentially subjected to delta aging treatment and delta solution treatment, wherein the temperature ofdelta aging treatment is 850-970 DEG C, and the temperature of delta solution treatment is 1015-1035 DEG C. In the method, delta aging treatment is carried out on the laser-repaired nickel-base high temperature alloy at first, and the Laves brittle phase is eliminated; and then delta solution treatment is carried out at the temperature of 1015-1035 DEG C for eliminating the delta phase separated out in the previous step. Since the temperature of delta solution treatment is lower than the solution temperature for eliminating the Laves phase in conventional heat treatment, damage caused by hightemperature solution on the alloy structure and the mechanical property can be avoided, and the mechanical property of the nickel-base high temperature alloy is obviously improved along with eliminating of the Laves phase.