CN104975234A 一种550MPa级非水冷热机械控制工艺钢及其生产方法 失效 - 权利终止 转让

一种550MPa级非水冷热机械控制工艺钢及其生产方法
摘要：
本发明提供的一种550MPa级非水冷热机械控制工艺钢及其生产方法，其中，所述工艺钢至少包括：0-0.08％的C、0-0.010％的P、0-0.005％的S、1.0％-1.5％的Mn、0.70％-1.0％的Si、0.2％-0.4％的Ni、1.0％-1.5％的Cr、0.5％-0.8％的Mo、1.2％-1.6％的Cu、0.06％-0.20％的V、0.01％-0.04％的Re和余量的杂质Fe。本发明实现了所形成的工艺钢的屈服强度≥550MPa，抗拉强度≥620MPa，-60℃时的冲击功≥100J。
摘要（英）：

The invention provides 550-MPa non-water-cooling thermomechanical control process steel and a production method thereof. The process steel at least comprises 0-0.08% of C, 0-0.010% of P, 0-0.005% of S, 1.0%-1.5% of Mn, 0.70%-1.0% of Si, 0.2%-0.4% of Ni, 1.0%-1.5% of Cr, 0.5%-0.8% of Mo, 1.2%-1.6% of Cu, 0.06%-0.20% of V, 0.01%-0.04% of Re and the balance impurity Fe. It is achieved that the yield strength of the formed process steel is greater than or equal to 550 MPa, the tensile strength is greater than or equal to 620 MPa, and the impact energy generated when the temperature is minus 60 DEG C is greater than or equal to 100 J.