Provided is a method for producing laminated glass, by which glass plates and an interlayer are sufficiently pressure-bonded even when two glass plates among a plurality of glass plates have different thicknesses, thereby enabling reduction in the distortion of the glass plates and suppression of deterioration of an outer appearance. A method for producing laminated glass by bending and forming glass plates heated to around a softening point comprises a forming step of mounting a plurality of glass plates (2, 4) stacked with a release agent therebetween on a ring die (20) and bending and forming the glass plates into a curved shape under the own weight thereof. In the forming step, at least two glass plates among the plurality of glass plates (12, 14) have different thicknesses, the thickness of the thinnest glass plate (14) is less than 1.6 mm, and the difference between the thickness of the thinnest glass plate (14) and the thickness of the thickest glass plate (12) is 0.5 mm or more, and in the forming step, the plurality of glass plates (2, 4) are bended and formed while being mounted on the ring die (20) such that the glass plate having a thinner thickness is disposed in a lower position.