Highly branched compositions including: (i) from about 96 wt % to about 99.9 wt % metallocene catalyzed ethylene propylene diene derived units; and (ii) from about 0.1 wt % to about 4 wt % multifunctional monomer derived units, wherein the highly branched composition has: (a) a Mooney viscosity ML (1+4) at 125° C. of about 30 to 100 MU, (b) a Mooney relaxation area MLRA of about 100 to about 1000, (c) a branching index, g′(vis) of less than about 0.9, (d) a phase angle, δ, of less than about 55 degrees at a complex modulus of 10 kPa, measured at 190° C., and (e) a degree of shear thinning greater than about 0.95, measured at 190° C., are disclosed herein. Homogeneous blends including this composition are also described. Processes to make the highly branched composition and the homogeneous blend are also described herein.