A producing method of direct reduced iron includes the steps of: drying an oxidized iron raw material selected from a group including iron ore and iron-making dust generated in an iron-making process to have a predetermined moisture content; mixing the oxidized iron raw material subjected to the drying step and a reducing material having a predetermined moisture content to obtain a mixture; pulverizing the mixture obtained in the mixing step for 80% minus-sieve to have a particle diameter of 70 μm to 500 μm; kneading the mixture after the moisture content of the mixture subjected to the pulverizing step is adjusted; agglomerating the mixture subjected to the kneading step to be agglomerate; and reducing the agglomerate obtained in the agglomerating step by a rotary hearth furnace to generate direct reduced iron.