The invention provides a double-ironing cyclic extrusion solidification method for remanufacturing titanium abandoned cuttings. The method includes the following steps of (1), recycling and pretreatment of the Ti cuttings, specifically, the Ti cuttings are cleaned for removing oil stains and impurities; (2), BM treatment of the Ti cuttings, specifically, the Ti cuttings pretreated in step (1) are subjected to ball milling; (3), sleeving and packaging of the BM-Ti cuttings, specifically, the BM-Ti cuttings are loaded into a copper barrel cavity, and then the cuttings are compressed preliminarily by a manual pressing machine; (4), room temperature cold squeezing of the sleeved and packaged BM-Ti cuttings; (5), double-ironing cyclic extrusion high-temperature solidification machining; (6), ejection and demoulding of a Ti material sample, specifically, an upper punch pin is removed, a pure-aluminum pseudo sample is placed in a die lower cavity, and a lower punch pin provides extension force to push the remanufactured Ti material obtained in step (5) for demoulding; (7), quenching, specifically, a block Ti material obtained in the ejection step (6) is quenched in a water cooling manner and cooled to the room temperature.