CN106479626A 一种封存防锈油及其制备方法 无效 - 驳回

一种封存防锈油及其制备方法
摘要：
本发明公开了一种封存防锈油及其制备方法，所述的制备方法包括下述的步骤：(1)将搅拌罐内温度升高至90-110℃，向搅拌罐内加入矿物油230-300份、磺基琥珀酸双十三烷酯钠5-12份、椰油基三甲基氯化铵4-9份、甲基丙烯酸二乙氨基乙酯2-4份、萜烯树脂2-5份，机械搅拌；(2)再将搅拌罐内温度升高至110-120℃，再向其中加入三羟甲基丙烷三丙烯酸酯3-6份、乙基苯基二硫代氨基甲酸锌2-5份、月桂酰二乙醇胺3-6份、十八醇4-8份、特丁基甲酚2-5份，再搅拌；(3)用高速剪切机对搅拌罐内成分进行高速剪切，冷却至室温，为封存防锈油。制备的防锈油具有制造工艺简单，适用范围广泛的特点。
摘要（英）：

The invention discloses sealing storage anti-rust oil and a preparation method thereof. The preparation method comprises the following steps of (1) rising the temperature in a stirring tank to 90 to 110 DEG C; adding 230 to 300 parts of mineral oil, 5 to 12 parts of C30H57O7S.Na, 4 to 9 parts of coco trimethyl ammonium chloride, 2 to 4 parts of 2-diethylaminoethyl methacrylate and 2 to 5 parts of terpene resin into the stirring tank; performing mechanical stirring; (2) raising the temperature in the stirring tank to 110 to 120 DEG C; then, adding 3 to 6 parts of trimethylolpropane triacrylate, 2 to 5 parts of zinc ethylphenyl dithiocarbamate, 3 to 6 parts of Lauryl diethanolamide, 4 to 8 parts of octadecanol and 2 to 5 parts of tert-butyl-cresol into the stirring tank; then, performing stirring; (3) performing high-speed shearing on ingredients in the stirring tank by a high-speed shearing machine; cooling the materials to the room temperature to obtain the sealing storage anti-rust oil. The prepared sealing storage anti-rust oil has the characteristics that the manufacturing process is simple; the application range is wide.

0/0