The invention discloses a vehicle pasted film. The vehicle pasted film sequentially comprises a film base material, a bonding layer and a release film layer from outside to inside, wherein the film base material is prepared from the following raw materials in parts by weight: 100 parts of PVC resin powder of which the polymerization degree is 1300, 8-12 parts of nanometer calcium carbonate, 25-30 parts of a plastifier DINP, 2-5 parts of an auxiliary plastifier namely soybean oil, 5-7 parts of a stabilizing agent and 2-3 parts of an antioxidant. Besides, the invention further discloses a production method of the vehicle pasted film. The production method comprises the following steps of (a) preparing the raw materials in proportion, and making the prepared raw materials into the film base material through a PVC film calendering technology; (b) scraping solvent-based glue to the film base material through a knife coating technology so as to obtain the bonding layer; (c) jointing the release film layer on the bonding layer so as to obtain the vehicle pasted film; and (d) performing edge trimming and breadth forming on the vehicle pasted film, and winding the treated vehicle pasted film into rolls. The vehicle pasted film disclosed by the invention is superior in properties, and has good mounting effects.