CN105478326A 一种封边条用木皮弹性哑光面漆UV涂装施工工艺 无效 - 驳回

一种封边条用木皮弹性哑光面漆UV涂装施工工艺
摘要：
一种封边条用木皮弹性哑光面漆UV涂装施工工艺，包括以下步骤S1、将成卷天然木皮或科技木皮基材使用木皮专用砂光机进行砂毛处理；S2、辊涂木皮专用弹性UV腻子，涂布量为30g/㎡，然后用双汞灯进行紫外线干燥，干燥强度为200mJ，干燥时间为3秒；S3、辊涂木皮专用弹性UV弹性底漆，涂布量为70g/㎡，然后用双汞灯进行紫外线干燥，干燥强度为200mJ，干燥时间为3秒；S4、辊涂木皮专用弹性UV砂光底漆，涂布量为30g/㎡，然后用双汞灯进行紫外线干燥，干燥强度为250mJ，干燥时间为3秒，等步骤。本发明的施工工艺无需喷涂，没有漆雾，而且能适用于批量生产；由于是UV油漆辊涂于基材表面，最主要的是使用弹性底漆和面漆涂装后的木皮包覆木线条后无需后续的涂装处理。
摘要（英）：

The invention discloses a half-open UV coating construction process of edge band veneer elastic matte finishing paint. The half-open UV coating construction process comprises the following steps: (S1) a coiled natural veneer or technical veneer base material is sanded by a special veneer sanding machine; (S2) the roll coating is performed for special veneer elastic UV putty; the coating quantity is 30 g/m2; double mercury lamps are used for ultraviolet drying; the drying strength is 200 mJ; and the drying time is 3 seconds; (S3) the roll coating is performed for special veneer elastic UV elastic primer; the coating quantity is 70 g/m2; then, double mercury lamps are used for ultraviolet drying; the drying strength is 200 mJ; and the drying time is 3 seconds; (S4) the roll coating is performed for special veneer elastic UV sanding primer; the coating quantity is 30 g/m2; then, double mercury lamps are used for ultraviolet drying; the drying strength is 250 mJ; and the drying time is 3 seconds; and the like. The construction process needs no spraying, is free of paint mist, and can be suitable for batch production; and as the roll coating is performed for UV paint on the surface of the base material, subsequent coating treatment is not needed after a wood line is coated by a veneer painted by the elastic primer and finishing paint.

0/0