CN104908392A 亮晶高光泽装饰软膜 有权

亮晶高光泽装饰软膜
摘要：
本发明涉及一种亮晶高光泽装饰软膜，所述装饰软膜包括面膜、中膜和底膜，所述面膜的原料为：聚合度1000的PVC树脂粉80～100重量份、环保增塑剂38～52重量份、钙锌稳定剂3～6重量份；中膜的原料为：聚合度1000的PVC树脂粉75～100重量份、环保增塑剂45～50重量份、钙锌稳定剂2～5重量份、亮晶片0.5～1.2重量份；底膜的原料为：聚合度1000的PVC树脂粉85～100重量份、环保增塑剂40～48重量份、钙锌稳定剂2～6重量份；色料3～7重量份；所述面膜、中膜和底膜采用一体贴合后经冷却定型、裁边定幅后制得，所述装饰软膜最后经收卷保存。本发明不仅具有光泽度高、视觉效果好等特点，而且具有拉伸强度高、断裂伸长率好、直角撕裂负荷以及静水压高等优点。
摘要（英）：

The invention relates to a sparkling high-gloss decoration flexible film. The decoration flexible film comprises a surface film, a middle film and a bottom film, and the surface film is made of 80-100 parts by weight of PVC resin powder with the polymerization degree of 1000, 38-52 parts by weight of an environmentally friendly plasticizer and 3-6 parts by weight of a calcium and zinc stabilizer; the middle film is made of 75-100 parts by weight of the PVC resin powder with the polymerization degree of 1000, 45-50 parts by weight of the environmentally friendly plasticizer, 2-5 parts by weight of the calcium and zinc stabilizer and 0.5-1.2 parts by weight of paillette; the bottom film is made of 85-1000 parts by weight of the PVC resin powder with the polymerization degree of 1000, 40-48 parts by weight of the environmentally friendly plasticizer, 2-6 parts by weight of the calcium and zinc stabilizer and 3-7 parts by weight of a pigment; and the decoration flexible film is made through integral lamination of the surface film, the middle film and the bottom film and trimming tentering, and is rolled and preserved. The decoration flexible film has the advantages of high glossiness, good visual effect, high tensile strength, good elongation at break, high right-angled tearing load and high hydrostatic pressure.

公开/授权文献
0/0