CN101311234B 一种金属闪光粉末涂料及制备方法 失效 - 权利终止

一种金属闪光粉末涂料及制备方法
摘要：
本发明提供了一种金属闪光粉末涂料，其包括闪光成分、树脂、填料和固化剂，其特征在于：所述的闪光成分1份；树脂5～10份；填料1～3份；固化剂0.4～0.8份；所述的闪光成分包括树脂和具有金属闪光效果粉末，并且将所述的具有金属闪光效果的粉末和树脂进行混合并加热、保温，使得所述的树脂充分熔化并和所述的具有金属闪光效果的粉末全部均匀融合在一起，接着对其冷却、压片、破碎、研磨、过筛得到闪光粉体组分；将所述的固化剂、树脂和填料经过挤出机挤出、压片、冷却、破碎、粉碎、过筛，接着与所述的闪光粉体组分进行混合得到的金属闪光粉末涂料，其具有更好的角度色品。
摘要（英）：

The invention provides a metal flash powder coating, comprising flash component, resin, stuffing and curing agent, and is characterized in that the components include 1 part of flash component, 5-10 parts of resin, 1-3 parts of stuffing and 0.4-0.8 parts of curing agent; wherein, the flash component comprises the resin and the powder with metal flashing effect; the powder with metal flashing effect is mixed with the resin, heated and insulated so as to allow the resin to be fully melt and to be fully and uniformly melt together with the powder with metal flashing effect, and then the flash powder component can be obtained through cooling, performing, scattering, grinding and screening. The curing agent, the resin and the stuffing are extruded by an extruder, preformed, cooled, crushed, shattered, crushed, screened and mixed with the flash powder component to obtain the metal flash powder coating. The coating of the invention has better angle chromaticity.

公开/授权文献
0/0