The invention relates to a method for preparing an anti liquid zinc corrosion wear material and a method for preparation, and belongs to the technology field of material corrosion and wear. The chemical components of the anti liquid zinc corrosion wear material are that carbon is 0.6-0.8 percent by weight, boron is 4.0-7.0 percent by weight, chromium is 4.0-6.0 percent by weight, molybdenum is 4.0-7.0 percent by weight, tungsten is 2.0-5.0 percent by weight, silicon is 0.3-0.6 percent by weight, manganese is 0.3-0.6 percent by weight, sulfur is less than 0.05 percent by weight, phosphorus is less than 0.05 percent by weight, and the allowance is ferric. The anti liquid zinc corrosion wear material of the invention uses an electric furnace to smelt, after being annealed, a casting is roughprocessed, after being quenched in 980-1020 DEG C and tempered in 520-580 DEG C, the casting is finally processed. The anti liquid zinc corrosion wear material of the invention has high hardness in normal temperature, the hardness is capable of reaching to 62-65, the hardness is also capable of reaching 56-58 in 500 DEG C, and the bending strength is 900-1100 MPa. When being eroded and worn, the invention has excellent using effects, and the life of stainless steel is improved by 3-6 times.